Estudo das propriedades mecÃnicas de ligas Fe-Ni e Fe-Ni-Mo processadas por metalurgia do pà / Study of Mechanical Properties of Alloy Fe-Ni And Fe-Ni-Mo Processed By Powder Metallurgy.

Os produtos feitos de ferro puro contendo Ni expandiram enormemente as aplicaÃÃes de produtos sinterizados, incluindo a fabricaÃÃo de peÃas que suportam altas cargas em automÃveis tais como transmissÃes. O diagrama de equilÃbrio de ligas Fe-Ni demonstram a presenÃa de fases α e FeNi3, porÃm as transformaÃÃes de fases necessitam de uma satisfatÃria homogeneizaÃÃo quÃmica, obtidas por processos convencionais de fabricaÃÃo de ligas por elevaÃÃo dos componentes ao estado lÃquido. Jà a sinterizaÃÃo por fase sÃlida facilita a formaÃÃo de clusters, uma vez que as partÃculas se unem sem mudanÃa de estado, o que implica em regiÃes cuja composiÃÃo quÃmica difere bastante da composiÃÃo global. Deste modo, este trabalho pretende contribuir com um estudo direcionado a identificaÃÃo de fases em ligas Fe-Ni e Fe-Ni-Mo sinterizadas a temperatura de 1100ÂC e processadas por moagem de alta energia (MAE), de forma a avaliar: a interface dissimilar formada entre os elementos, analisar os fenÃmenos encontrados na mesma e identificar caracterÃsticas metalÃrgicas apÃs a sinterizaÃÃo que contribuam para aumento da dureza, microdureza, limite de resistÃncia a traÃÃo e mÃdulo de elasticidade. O estudo apresentarà a determinaÃÃo do diagrama de equilÃbrio atravÃs do software ThermoCalc, tÃcnicas de difraÃÃo por raios X e espectrometria de raios X por energia dispersiva (EDS), alÃm de anÃlises de microscopia optica e microscopia eletrÃnica de varredura (MEV). Os resultados mostraram a presenÃa das fases estÃveis como α(CCC) e fase metaestÃveis como FeNi (CFC Austenita). As anÃlises microscÃpicas demonstram tambÃm uma heterogeneidade com diferentes percentuais de NÃquel e Ferro ao longo das amostras. / The products made of pure iron containing Ni greatly expanded the applications of sintered products , including the manufacture of parts that withstand high loads such
as transmissions in cars . The equilibrium diagram of Fe-Ni alloys demonstrate the presence of α and FeNi3 phase , but the phase transformations require a satisfactory chemical homogenization obtained by conventional processes for production of alloys by elevation of the liquid components .The solid-phase sintering facilitates the formation of clusters , since the particles together without change of state, which implies regions whose chemical composition differs significantly from the overall composition . Thus , this paper aims to contribute to a study aimed at identifying phases in alloys Fe - Ni and Fe - Ni - Mo sintered at temperature of 1100 Â C and processed by high energy ball milling ( RBM ) in order to assess the following: interface formed between dissimilar elements , analyze the phenomena found in it and identify
metallurgical characteristics after sintering contributing to increased hardness, microhardness , ultimate tensile strength and modulus of elasticity . The study shall determine the equilibrium diagram through Thermocalc software , diffraction , X-ray spectrometry and X-ray energy dispersive ( EDS ) , and the analysis of optical
microscopy and scanning electron microscopy (SEM ) . The results showed the presence of stable phases as α (CCC) and metastable phase as FeNi (CFC austenite). The microscopic analysis also demonstrated heterogeneity with different percentages of Nickel and Iron along the samples.

Identiferoai:union.ndltd.org:IBICT/oai:www.teses.ufc.br:8109
Date30 May 2014
CreatorsCandido Jorge de Sousa Lobo
ContributorsMarcelo Josà Gomes da Silva, Ricardo EmÃlio Ferreira Quevedo Nogueira, Jeferson Leandro Klug, Wanderley Ferreira de Amorim Junior, Marcelo Camargo Severo de MacÃdo
PublisherUniversidade Federal do CearÃ, Programa de PÃs-GraduaÃÃo em Engenharia e CiÃncia de Materiais, UFC, BR
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis
Formatapplication/pdf
Sourcereponame:Biblioteca Digital de Teses e Dissertações da UFC, instname:Universidade Federal do Ceará, instacron:UFC
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0019 seconds