The thesis is focused on the theoretical description of the technology of anodizing of aluminium, magnesium, zinc and their alloys. In this work, methods for formation of oxide layers and the used chemical processes are described in detail. The experimental part of this work deals with formation of oxide layers on aluminium, magnesium and zinc of high purity under different conditions. Oxide layers of different thicknesses were created on all three experimental materials. Aluminium was anodized in a bath of 10% H2SO4, magnesium in the bath of 1 mol/dm3 NaOH, and zinc in the bath of 0.5 mol/dm3 NaOH. Processes were carried out at laboratory temperature. On the aluminium, continuous oxide layer was formed. Furthermore rule "312" was verified, that can indicatively be used for calculating the thickness of the resulting oxide layer on the aluminium. When using lower current of 0.08 and 0.2 A for magnesium anodizing, dark colored layer was created comparing to higher current of 0.5 A. More rough appearance of the oxide layer was produced with increasing voltage. Further, it was observed for magnesium that the resulting layer comprises of two sublayers. For zinc, black colored layer was created when the voltage 20 V and current from 0.4 to 0.5 A were used. In the layer, two sublayers were also observed. For lower voltage and current (0.05 A, 0.17 V), formation of the oxide layer on the zinc does not occur, but the crystallographic etching was observed.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:231773 |
| Date | January 2015 |
| Creators | Remešová, Michaela |
| Contributors | Hadraba,, Hynek, Čelko, Ladislav |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0019 seconds