Fabrications and Characterization of Nonvolatile Memory Devices with Zn nano Thin Film Embedded in MIS Structure

Non-volatile memory is slower than DRAM (Dynamic Random Access Memory) but faster than HDD (Hard Disk Drive). In addition, compared to volatile memory, the non-volatile memory can retain stored information without power, and consume only low power. These characteristics show its popularity of flash memory built in portable devices. Currently the non-volatile memory applies the polysilicon and SONOS structure as floating gate, however, the new technologies of nanocrystal non-volatile memory are processed at high temperature. The manufacturing cost is rather high, so the process at lower temperature is very necessary. In this work, mixed zinc and silica amorphous layers are applied as floating gate to construct nano thin film non-volatile memory devices. The process does not need high temperature to form crystalline, and the defects in zinc oxide can be applied for charge storage. Supercritical carbon dioxide (SCCO2) treatment has been studied for the passivation of dielectric and reducing the activation energy. Using this low-temperature SCCD process ZnO nanocrystal can be formed, and the feasibility of fabricating nanocrystal NVMs device with low temperature SCCO2 is possible. The nonvolatile memory devices with Zn nano thin film embedded in MIS structure are performed. From C-V measurement, it is found that defects in SiO2 are repaired after 500¢J annealing. Because of the thermal diffusion, the storage layer SiO2/Zn-SiO2/SiO2 in device cannot be observed and the memory window disappears when the annealing temperature is higher than 700¢J. Therefore, the annealing process should be performed between 500¢J - 700¢J in making memory device. From DLTS analysis, a species with energy level of 0.6 eV is found in the as deposited Zn-SiO2 layer. After annealing in Ar, a new energy level 0.47 eV is found, and which shifts to energy level 0.85 eV after annealing in O2. In comparison to XPS results, traps of Zn-SiO2 exist before annealing, and after annealing in Ar, Zn-SiO2 transforms into Zn-O-Si. Traps of ZnO-SiO2 have been found after annealing in O2, which increases the memory effect with a 2 Volt memory window, so that more charges can be stored in the deep level traps of ZnO-SiO2 in the storage layer.

Identiferoai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0614110-163833
Date14 June 2010
CreatorsChen, Chao-yu
ContributorsTsung-ming Tsai, Tai-Fa Young, Chien-Hsiang Chao
PublisherNSYSU
Source SetsNSYSU Electronic Thesis and Dissertation Archive
LanguageCholon
Detected LanguageEnglish
Typetext
Formatapplication/pdf
Sourcehttp://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0614110-163833
Rightsnot_available, Copyright information available at source archive

Page generated in 0.002 seconds