The chemistry and corrosion mechanisms associated with reduced sulfur compounds such as calcium sulfide, present in ground granulated blast-furnace slag (GGBFS), have been studied in high-density concrete, mortar and simulated pore-water environments. The high-density concrete and mortar samples were produced to replicate the high-density GGBFS concrete, in the dry storage containers (DSCs), used for radiation shielding from used nuclear fuel. Electrochemical measurements on embedded steel electrodes in high-density GGBFS concrete and mortar samples, showed that sulfide is capable of consuming oxygen to create a stable, reducing environment, though not in all cases, and the high-frequency electrolyte resistance increases with hydration time. Ion chromatography on simulated pore-water environments determined that thiosulfate is quite kinetically stable as a sulfide oxidation product and magnetite is capable of oxidizing sulfide. Microscopy has also been used to provide visual evidence of GGBFS hydration and elemental quantification of the hydrating microstructure in different environments.
| Identifer | oai:union.ndltd.org:LACETR/oai:collectionscanada.gc.ca:OTU.1807/31361 |
| Date | 15 December 2011 |
| Creators | Nadarajah, Parthiban |
| Contributors | Newman, Roger C. |
| Source Sets | Library and Archives Canada ETDs Repository / Centre d'archives des thèses électroniques de Bibliothèque et Archives Canada |
| Language | en_ca |
| Detected Language | English |
| Type | Thesis |
Page generated in 0.0025 seconds