Carbon-doped aluminium oxide, α-Al₂O₃:C, is a ultra-sensitive dosimeter of topical research interest. The aim of this project was to investigate the dynamics of luminesce in this material. The methods of investigation consisted of thermoluminescence and time-resolved optical stimulation. Thermoluminescence measurements provide information on trap distribution and kinetic parameters of the traps involved in luminescence whereas time-resolved optical stimulation is a handy technique in investigation of luminescence lifetimes and provides an insight into the charge transitions between traps and recombination centres. Measurements were made on samples annealed at a nominal temperature of 900⁰C for 15 minutes. The material shows the presence of five thermoluminescence peaks at 37⁰C, 160⁰C, 300⁰C 410⁰C, and 480⁰C at a heating rate of 0.03k/s when irradiated to 6.0 Gy of beta. The main peak at 160⁰C, shows a linear dose response for doses between 0.1 Gy and 10 Gy and then goes sublinear above 10 Gy, the peak at 37⁰C shows a sublinear dose response for doses between 0.1 Gy and 10 Gy and appears to saturate thereafter, whereas the dose response of the peak at 300⁰C goes from linear to supralinear then apparently quadratic behaviour in the dose range of 0.1 Gy to 16.0 Gy. The trap depth of the main peak, that is, its activation energy as determined below the conduction band, has been approximated at 1.3 eV with a kinetic order of approximately 1.2. Time-resolved optical stimulation has been used to investigate luminescence lifetimes. The mean luminescence lifetime obtained for the sample at ambient temperatures is 35.0±1.0 ms. The investigations of the dependence of luminescence lifetimes on measurement temperature show that the material suffers from thermal quenching effects at measurement temperatures above 140⁰C with the activation energy of thermal quenching estimated at 1.045±0.002 eV. Shallow traps i.e. traps lying close to the conduction band, seem to elongate the lifetimes of optically stimulated luminescence in the material at temperatures between 30⁰C - 80⁰C due to charge retrapping. The material exhibits both fading and recuperation of the optically stimulated luminescence signal with storage time.
| Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:rhodes/vital:5447 |
| Date | January 2013 |
| Creators | Nyirenda, Angel Newton |
| Publisher | Rhodes University, Faculty of Science, Physics and Electronics |
| Source Sets | South African National ETD Portal |
| Language | English |
| Detected Language | English |
| Type | Thesis, Masters, MSc |
| Format | 109 leaves, pdf |
| Rights | Nyirenda, Angel Newton |
Page generated in 0.0017 seconds