Análise microestrutural e da resistência à fadiga de zircônia monolítica submetida a protocolos de ajuste simulado /

Orientador: Marco Antonio Bottino / Coorientadora: Lilian Costa Anami / Banca: Guilherme de Siqueira Ferreira Anzaloni Saavedra / Banca: Fernanda Campos / Resumo: O objetivo deste trabalho foi investigar as propriedades microestruturais e a resistência à fadiga de amostras de zircônia parcialmente estabilizada por óxido de ítrio (Y-TZP) para uso em forma monolítica (Vita YZ HT, Vita Zahnfabrik, Alemanha) após diferentes protocolos de ajuste clínico simulado. 162 discos de Y-TZP HT (12 mm de diâmetro, 0,8 mm de altura) foram confeccionados e aleatoriamente divididos em 6 grupos de acordo com as simulações (n=27): S- Y-TZP sinterizada (sem desgaste, sem glaze); G- Y-TZP sinterizada (sem desgaste) e glazeada; PdG- ajuste simulado da Y-TZP com ponta diamantada seguido por aplicação de glaze; GPd- ajuste simulado com ponta diamantada da Y-TZP já glazeada; PdBdG- ajuste simulado com ponta diamantada, seguido por borracha diamantada e aplicação do glaze; GPdBd- ajuste simulado com ponta diamantada, seguido por borracha diamantada da Y-TZP já glazeada. Após teste monotônico sob flexão biaxial (n=3, célula de carga de 1000 kgf, velocidade de 1 mm/min), os espécimes restantes foram distribuídos na proporção 3:2:3 e testados sob fadiga acelerada (step stress) em três perfis de carregamento (leve, moderado e agressivo), variando-se os incrementos de carga e número de ciclos. Os espécimes representativos fraturados foram avaliados em estereomicroscopio e microscópio eletrônico de varredura (MEV) e as características microestruturais das superfícies obtidas com os diferentes protocolos foram analisadas quanto a difração de raios-X, rugosidade média ... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The objective of this study was to investigate the microstructural properties and fatigue resistance of zirconia partially stabilized by yttrium oxide (Y-TZP) for use in monolithic form (Vita YZ HT, Vita Zahnfabrik, Germany) after different clinical adjustment protocols simulation. 162 disc of Y-TZP HT (12 mm diameter, 0.8 mm high) were made and randomly divided into 6 groups according to the adjustment protocol (n = 27): S- Y-TZP as sintered (without adjustment and glaze); G- glazed Y-TZP (without adjustment); PdG- Y-TZP with adjustment simulation procedure with diamond bur followed by glaze application; GPd- glazed Y-TZP followed by adjustment simulation procedure with diamond bur; PdBdG- Y-TZP with adjustment simulation procedure with diamond bur and polishing kit, followed by glaze application; GPdBd- glazed Y-TZP with adjustment simulation procedure with bur followed by polishing kit. After monotonic testing under biaxial flexure (n=3, 1000 kgf load cell, 1 mm/min speed), the remaining specimens were distributed into 3:2:3 ratio and tested under step-stress in three profiles (light, moderate and aggressive), varying the load, increments and number of cycles. The fractured representative specimens were evaluated in a stereomicroscope and scanning electron microscope (SEM) and the microstructural characteristics of the surfaces obtained with different protocols were analyzed by X-ray diffraction, mean roughness (Ra), profilometry and SEM. Survival or fracture data were used to calculate Weibull's beta (β) value and reliability for 300,000 and 600,000 cycles at 200 N. The spectra obtained by the diffraction were compared with standard spectra from databases. Ra data were statistically analyzed by 1-way ANOVA and Tukey's test (both, a=5%). The images were analyzed and qualitatively described. There was no significant change in zirconia crystallography ....(Resumo completo, clicar acesso eletrônico abaixo) / Mestre

Identiferoai:union.ndltd.org:UNESP/oai:www.athena.biblioteca.unesp.br:UEP01-000883905
Date January 2017
CreatorsChun, Eliseo Pablo.
ContributorsUniversidade Estadual Paulista "Julio de Mesquita Filho" Instituto de Ciência e Tecnologia (Campus de São José dos Campos).
PublisherSão José dos Campos,
Source SetsUniversidade Estadual Paulista
LanguagePortuguese, Portuguese, Texto em português; resumos em português e inglês
Detected LanguagePortuguese
Typetext
Format51 f.
RelationSistema requerido: Adobe Acrobat Reader

Page generated in 0.0028 seconds