Made available in DSpace on 2015-01-26T13:21:26Z (GMT). No. of bitstreams: 0
Previous issue date: 2003-08-07Bitstream added on 2015-01-26T13:30:28Z : No. of bitstreams: 1
000208860.pdf: 3521446 bytes, checksum: f0a31580cbd6c2c3aca55e96161e38eb (MD5) / O objetivo deste estudo in vitro foi avaliar o efeito de diferentes tratamentos da superfície cerâmica, na resistência ao cisalhamento da união entre porcelana e cimento resinoso. Foram confeccionados sessenta pares de discos de porcelana aluminizada a 50% Vitadur Alpha (Vita), de tamanhos padronizados em 6mm de diâmetro por 3mm de espessura (A), e 3mm por 3mm (B). As amostras foram divididas aleatoriamente em seis grupos (n=10), de acordo com um dos seguintes tratamentos de superfície: condicionamento com ácido fluorídrico por 2 e 4min (G1 e G2), jateamento com óxido de alumínio (50µm) por 5s (G3), jateamento seguido de ácido fluorídrico por 2 e 4min (G4 e G5) e controle (G6). Em seguida, foi aplicado silano (Tokuso Ceramic Primer - Tokuyama) na superfície tratada de ambos os discos, e os discos B foram cimentados sobre os respectivos discos A, utilizando cimento resinoso dual (Bistite ll DC- Tokuyama). Os espécimes foram armazenados em água destilada a 37ºC por 24h, para posterior teste de cisalhamento em máquina de ensaio universal. Os resultados obtidos, expressos em MPa, foram submetidos aos testes de ANOVA fator único e Tukey (p≤0,05). O condicionamento com ácido fluorídrico por 2min apresentou resultados significantemente superiores ao condicionamento por 4min e ao grupo controle, porém não diferiu estatisticamente do jateamento, associado ou não ao ácido fluorídrico por 2 ou 4min / The aim of this ln vitro study was to evaluate the effect of different surface treatments on the shear bond strength between porcelain and resin cement. Sixty pairs of 50% aluminous porcelain (Vitadur Alpha - Vita) discs were fabricated, each with 6mm in diameter by 3mm in thickness (A), and 3 by 3mm (B). Samples were randomly divided into six groups (n=10), according to one of the following surface treatments: etching with 10% hydrofluoric acid for 2 or 4min (G1 and G2); sandblasting with aluminum oxide (50µm) for 5s (G3); sandblasting followed by etching for 2 or 4min (G4 e G5) and control (G6). Then, silane was applied (Tokuso Ceramic Primer- Tokuyama) on the treated surface of both discs, and using a dual-cure resin cement (Bistite ll DC- Tokuyama), B discs were bonded together with their respective A discs. Specimens were stored in distilled water at 37ºC for 24h before shear bond strength were determined on a universal testing machine. The results, in MPa, were compared by one-way ANOVA and Tukey test (p≤0,05). Bond strength produced alter etching with 10% hydrofluoric acid for 2min was significantly higher than etching for 4min and control, but there was no statistical difference to sandblasting a/one, or followed by etching for 2 or 4min
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/113974 |
| Date | 07 August 2003 |
| Creators | Nagayassu, Marcos Paulo [UNESP] |
| Contributors | Universidade Estadual Paulista (UNESP), Araújo, José Eduardo Junho de [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 122 f. : il. anexo |
| Source | Aleph, reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | -1, -1 |
Page generated in 0.0077 seconds