In the present work, phase transformations in TIMETAL LCB tita- nium alloy and their influence on mechanical properties were studied. Different initial conditions were prepared by solution treating above β-transus immedi- ately followed by heat treatment in α/β temperature regime. These resulted in different grain boundary α thicknesses and contiguities at a fixed α vol- ume fraction. The subsequent ageing response of this material was studied by low temperature ageing at 400 ◦ C, 450 ◦ C and 500 ◦ C. Phase transformations were studied by X-ray diffraction (XRD), scanning electron microscopy (SEM), differential scanning calorimetry (DSC) and resistivity measurements. Mechan- ical properties were investigated using microhardness measurements and tensile tests. It has been proved that metastable ω phase is formed during annealing at 400 ◦ C and 450 ◦ C. ω particles further transform to very fine precipitates of α phase when exposed to annealing for longer time periods. These fine precip- itates significantly contribute to increase of microhardness and achieving high value of yield stress. Keywords: Metastable beta Ti alloys, phase transformations, microstructure changes, ω phase 1
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:308700 |
| Date | January 2012 |
| Creators | Šmilauerová, Jana |
| Contributors | Janeček, Miloš, Šíma, Vladimír |
| Source Sets | Czech ETDs |
| Language | English |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.017 seconds