Optical properties of Tl4In3GaSe8, Tl4InGa3Se8, Tl4In3GaS8, Tl2InGaS4 and Tl4InGa3S8 chain and layered crystals were studied by means of photoluminescence (PL) and transmission-reflection experiments. Several emission bands were observed in the PL spectra within the 475-800 nm wavelength region. The results of the temperature- and excitation intensity-dependent PL measurements in 15-300 K and 0.13× / 10-3-110.34 W cm-2 ranges, respectively, suggested that the observed bands were originated from the recombination of electrons with the holes by realization of donor-acceptor or free-to-bound type transitions. Transmission-reflection measurements in the wavelength range of 400-1100 nm revealed the values of indirect and direct band gap energies of the crystals studied. By the temperature-dependent transmission measurements in 10-300 K range, the rates of change of the indirect band gap of the samples with temperature were found to be negative. The oscillator and dispersion energies, and zero-frequency refractive indices were determined by the analysis of the refractive index dispersion data using the Wemple&ndash / DiDomenico single-effective-oscillator model. Furthermore, the structural parameters of all crystals were defined by the analysis of X-ray powder diffraction data. The determination of the compositional parameters of the studied crystals was done by energy dispersive spectral analysis experiments.
Identifer | oai:union.ndltd.org:METU/oai:etd.lib.metu.edu.tr:http://etd.lib.metu.edu.tr/upload/12609442/index.pdf |
Date | 01 April 2008 |
Creators | Goksen, Kadir |
Contributors | Hasanli, Nizami Mamed |
Publisher | METU |
Source Sets | Middle East Technical Univ. |
Language | English |
Detected Language | English |
Type | Ph.D. Thesis |
Format | text/pdf |
Rights | To liberate the content for public access |
Page generated in 0.0017 seconds