Previous issue date: 2017-10-04 / Capes / O presente trabalho tem o intuito tecnológico da concepção e análise de uma superfície com alto rendimento térmico e com resistência a corrosão em amostras a simular um concentrador solar, parte integrante de um coletor solar. O coletor solar desenvolvido pela Suna Engenharia é um dispositivo sustentável que promove o aquecimento de um fluido, água ou ar, através da conversão da radiação eletromagnética do sol em energia térmica. Seu alcance térmico é em torno de 60°C, para aprimorar o rendimento térmico do equipamento é necessário inferir a característica de superfície seletiva, que determina alta absorção e baixa emissão da radiação óptica espectral. Para o desenvolvimento deste projeto, a superfície a simular o concentrador solar, incluiu-se como vertentes os parâmetros a serem analisados: substrato (aço Inoxidável 304, 316 e aço Carbono 1020), depósito metálico (banhos galvânicos de ligas binárias ZnNi e ZnFe), método de tratamento de superfície (galvânização por eletrodeposição), e variadas espessuras (a serem obtidas pelo Método Coulométrico). Através de análises de ampliações ópticas (MEV, EDS e Microscopia Óptica), de absorbância (Espectrofotometria por FTIR) e de resistência a corrosão (Rp, Corrosimetria e EVT) foi possível selecionar os parâmetros que forneceram os melhores resultados das amostras, em atribuições aferidas se destacou o depósito galvânico de liga binária ZnNi no substrato de aço inox 304, sob espessura de 15 μm. / The present work has the technological aim of designing and analyzing a surface with high thermal efficiency and resistance to corrosion in samples simulating a solar concentrator, an integral part of a solar collector. The solar collector developed by Suna Engenharia is a sustainable device that promotes the heating of a fluid, water or air, by converting the electromagnetic radiation from the sun to thermal energy. Its thermal reach is around 60 ° C, to improve the thermal performance of the equipment it is necessary to infer the selective surface feature, which determines high absorption and low emission spectral optical radiation. For the development of this project, the surface to be simulated the solar concentrator, the parameters to be analyzed were included as slopes: substrate (stainless steel 304, 316 and carbon steel 1020), metallic deposit (galvanic baths of binary alloys ZnNi and ZnFe), surface treatment method (galvanizing by electrodeposition), and various thicknesses (to be obtained by the Coulometric Method). Through the analysis of optical amplification (SEM, EDS and Optical Microscopy), absorbance (FTIR spectrophotometry) and corrosion resistance (Rp, Corrosimetry and EVT), it was possible to select the parameters that provided better results, verified assignments in the highlighted the ZnNi binary alloy galvanic deposit on the 304 stainless steel substrate, under a thickness of 15 μm.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/545 |
| Date | 30 April 2018 |
| Creators | SOUSA, Márcia Cristina de. |
| Contributors | VILAR, Eudésio Oliveira., SILVA, José Nilton., CUNHA, Carlos Thiago Cândido. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM ENGENHARIA QUÍMICA, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0155 seconds