Ordered mesoporous silicas have been shown to have a variety of useful applications ranging from adsorbents for containments to supports for catalysts. While these materials have received a good deal of attention in the literature there is still much opportunity for new technologies. We present research describing a novel approach to incorporate functionality onto the pore surfaces of these materials as well as a highly active catalyst for the Suzuki-Miyaura reaction.
Our approach to selectively graft functionality on to the pore walls of the mesoporous silicas SBA-15 and MCM-41 involves treating the materials loaded with a structure directing agent (SDA), with hexamethyldisilazane that passivates the external surface through silylation. Once the SDA is removed the mesopores can be functionalized selectively using standard methods. A test designed to look at the passivation layer is also described.
The catalyst developed is designated Pd-SBA-15-SH(g) and it is active for the Suzuki-Miyaura reaction. The activity, recyclability and leaching of Pd-SBA-15-SH(g) was found to be superior to related materials. A mechanistic analysis suggests the catalyst is a reservoir for soluble Pd metal.
A key challenge that is holding back wide scale application of ammonia borane (NH3BH3) as a hydrogen storage material for mobile applications is the dearth of regeneration strategies. Presented are our forays into the development of an organic hydride based regeneration strategy. The first phase of the project focused on the reaction between Hantzsch esters and B(C6F5)3. N-substituted Hantzsch esters were found to transfer hydride to boron in >90 % yield. Mechanistic analysis of the reaction suggests either a SET mechanism or a highly asynchronous transition state. A novel hydride transfer equilibrium promoted by B(C6F5)3 was observed and it operated at temperatures below -10 ºC.
N,N-ditertbutyl-dihydroimidazole is also an effective hydride donor to B(C6F5)3 as well as other Lewis acids that are more relevant mimics to those invoked in regeneration schemes. When the redistribution of B(SPh)3 is carried out with N,N-ditertbutyl-dihydroimidazole in the presence of NEt3 and CH2Cl2 at 50 ºC, BH2(NEt)3(SPh) is formed. CH2Cl2 functions as a thiol scavenger under the reaction conditions. 1-Octene trapping experiments provided indirect evidence for the formation of diborane, a critical component in the regeneration of NH3BH3. / Thesis (Ph.D, Chemistry) -- Queen's University, 2011-09-09 14:51:54.697
| Identifer | oai:union.ndltd.org:LACETR/oai:collectionscanada.gc.ca:OKQ.1974/6712 |
| Date | 12 September 2011 |
| Creators | WEBB, JONATHAN DOUGLAS |
| Contributors | Queen's University (Kingston, Ont.). Theses (Queen's University (Kingston, Ont.)) |
| Source Sets | Library and Archives Canada ETDs Repository / Centre d'archives des thèses électroniques de Bibliothèque et Archives Canada |
| Language | English, English |
| Detected Language | English |
| Type | Thesis |
| Rights | This publication is made available by the authority of the copyright owner solely for the purpose of private study and research and may not be copied or reproduced except as permitted by the copyright laws without written authority from the copyright owner. |
| Relation | Canadian theses |
Page generated in 0.0033 seconds