Sílica gel quimicamente modificada com epicloridrina na presença ou ausência de solvente = estudo termodinâmico da interação envolvendo o cobre / Chemically modified silica gel with epichlorohydrin in presence or absence of solvent : termodynamic study involving copper interaction

Orientador: Claudio Airoldi / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Química / Made available in DSpace on 2018-08-20T09:35:04Z (GMT). No. of bitstreams: 1
Silva_IrleneMariaPereirae_M.pdf: 2812788 bytes, checksum: 83395128353119e4c0fa5e54a5e9748a (MD5)
Previous issue date: 2012 / Resumo: O polímero inorgânico sílica gel foi usado como suporte em reações de modificações de superfície, devido à presença de grupos silanol (Si-OH) na superfície, que confere grande reatividade em processo de imobilização. A superfície da sílica gel foi organofuncionalizada com epicloridrina a partir de uma nova rota sem a presença de silano ou solvente, reduzindo assim o impacto ambiental e o custo da reação. Este método, denominado de "rota sem solvente¿, foi otimizado com a realização de um planejamento experimental 2, variando o tempo da reação, a temperatura e o volume de epicloridrina utilizado. Para fins de comparação, a sílica gel também foi funcionalizada com epicloridrina a partir de duas rotas convencionais: a homogênea e a heterogênea, utilizando tolueno como solvente, 3-aminopropiltrietoxissilano como silano, além da epicloridrina. Para aumentar a disponibilidade de sítios básicos, foi adicionada uma nova cadeia orgânica a partir da reação com a dietanolamina para favorecer a sorção de cobre. Os produtos destas reações foram denominados de SiDM, SiDT e SiD, para as rotas homogênea, heterogênea e sem solvente, respectivamente. As sílicas obtidas foram caracterizadas por de análise elementar, espectroscopia na região do infravermelho, ressonância magnética nuclear no estado sólido para os núcleos de carbono e silício, e termogravimetria. Foram determinadas as capacidades de sorção dos íons de cobre (sorbato) através das sílicas modificadas (sorvente) obtidas pelas rotas homogênea, SiDM, heterogênea, SiDT, e sem solvente, SiD. A primeira sílica apresentou maior capacidade de sorção, 0,32 mmol g, seguida pelas sílicas SiD e SiDT com os valores de capacidade de sorção de 0,27 e 0,11 mmol g. A sílica obtida sem solvente satisfaz melhor o compromisso com a Química Verde. Sua capacidade de sorção superou SiDT, mesmo tendo um centro básico de nitrogênio a menos em relação as sílicas funcionalizadas com silano. As grandezas termodinâmicas calculadas a partir da titulação calorimétrica e batelada mostraram que em todos os sistemas estudados a interação entre os íons de cobre com os centros básicos na interface sólido/líquido é energeticamente favorável, pois apresentaram valores negativos de energia de Gibbs e entalpia exotérmica, e valores positivos de entropia, exceto para SiDM. Apesar desse valor de entropia negativo, ele não tornou o processo desfavorável / Abstract: The inorganic polymer silica gel was used as support of reactions on surface modifications due to the presence of silanol (Si-OH) groups that confers greater reactivity in immobilization process. The silica gel surface was organofunctionalized with epichlorohydrin from a new route without the presence of silane or solvent, thus reducing the environmental impact and cost of the reaction. This method, called "absence solvent route¿ was optimized with the realization of an experimental planning 2, varying reaction time, temperature and amount of epichlorohydrin. For comparison, the silica gel was functionalized with epichlorohydrin also from two conventional routes: a homogeneous and heterogeneous, using toluene as solvent, 3-aminopropyltriethoxysilane and epichlorohydrin. To increase the availability of basic sites it was added a new organic chain from a reaction with diethanolamine, to favor the sorption of copper. The products of these reactions were named SIDM, SIDT and SiD for the homogeneous, heterogeneous and absence solvent routes, respectively. All silicas were characterized by elemental analysis, infrared spectroscopy, nuclear magnetic resonance in solid state for carbon and silicon nuclei and thermogravimetry. The sorption capacity of copper ions (sorbate) using the modified silicas (sorbent) obtained by the homogeneous, SIDM, heterogeneous SIDT, and without solvent, SiD, routes was determined. The first silica showed higher sorption capacity 0.31 mmol g, followed by SiD and SIDT silicas, as 0.27 and 0.11 mmol g. The silica obtained without solvent performs the best agreement to green chemistry. The sorption capacity of SIDT silica surpassed even having one basic nitrogen center less than that one functionalized with silane. The calculated thermodynamic properties from calorimetric titration and batch wire process showed that for all studied systems the interaction between copper ions with basic centers at the solid/liquid interface is energetically favorable, since they have negative Gibbs energies and exothermic enthalpies, and positive entropy values, except with SiDM. In despite of entropy with negative value, it did not make the process unfavorable / Mestrado / Quimica Inorganica / Mestra em Química

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/250043
Date20 August 2018
CreatorsSilva, Irlene Maria Pereira e, 1982-
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Airoldi, Claudio, 1942-, Cavalheiro, Eder Tadeu Gomes, Mazali, Italo Odone
Publisher[s.n.], Universidade Estadual de Campinas. Instituto de Química, Programa de Pós-Graduação em Química
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Format98 p. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0029 seconds