Effective Properties of Randomly Oriented Kenaf Short Fiber Reinforced Epoxy Composite

Natural fibers have drawn attention of researchers as an environmentally-friendly alternative to synthetic fibers. Developing natural fiber reinforced bio-composites are a viable alternative to the problems of non-degrading and energy consuming synthetic composites. This study focuses on (i) the application of kenaf fiber as a potential reinforcement and, (ii) determining the tensile properties of the randomly oriented short kenaf fiber composite both experimentally and numerically. Kenaf fiber micro-structure and its Young's modulus with varying gage length (10, 15, 20, and 25.4 mm) were investigated. The variation in tensile strength of kenaf fibers was analyzed using the Weibull probability distribution function. It was observed that the Young's modulus of kenaf fiber increased with increase in gage length. Fabrication of randomly oriented short kenaf fiber using vacuum bagging techniques and hand-lay-up techniques were discussed and the tensile properties of the specimens were obtained experimentally. The tensile modulus of the composite sample at 22% fiber volume fraction was found to be 6.48 GPa and tensile strength varied from 20 to 38 MPa. Numerical models based on the micro mechanics concepts in conjunction with finite element methods were developed for predicting the composite properties. A two-step homogenization procedure was developed to evaluate the elastic constants at the cell wall level and the meso-scale level respectively. Von-Mises Fisher probability distribution function was applied to model the random orientation distribution of fibers and obtain equivalent modulus of composite. The predicted equivalent modulus through numerical homogenization was in good agreement with the experimental results.

Identiferoai:union.ndltd.org:UTAHS/oai:digitalcommons.usu.edu:etd-5599
Date01 May 2015
CreatorsL., Dayakar Naik
PublisherDigitalCommons@USU
Source SetsUtah State University
Detected LanguageEnglish
Typetext
Formatapplication/pdf
SourceAll Graduate Theses and Dissertations
RightsCopyright for this work is held by the author. Transmission or reproduction of materials protected by copyright beyond that allowed by fair use requires the written permission of the copyright owners. Works not in the public domain cannot be commercially exploited without permission of the copyright owner. Responsibility for any use rests exclusively with the user. For more information contact Andrew Wesolek (andrew.wesolek@usu.edu).

Page generated in 0.0018 seconds