Previous issue date: 2015-08-31 / Na odontologia os implantes dentários osseointegráveis têm sido a melhor opção para o tratamento da perda dental. Estes permitem a recuperação estética e funcional, como a capacidade de mastigação. Atualmente vem se introduzindo a utilização de polímeros para fabricação de implantes osseointegráveis em substituição aos convencionais de titânio, a exemplo do poli-éter-éter-cetona (PEEK). Dessa forma, o objetivo deste trabalho é avaliar as propriedades do PEEK para aplicações odontológicas a partir das caracterizações morfológica, química e físicas, na perspectiva de uso como implante. As amostras foram analisadas através de Microscopia Eletrônica de Varredura – MEV com Espectroscopia por Energia Dispersiva de raios X – EDS, Difração de raios-X (DRX), Espectroscopia na Região de Infravermelho com Transformada de Fourier (FTIR), Calorimetria Exploratória Diferencial (DSC) e Molhabilidade por Ângulo de Contato. O resultado de MEV apresentou característica de um material de superfície lisa e densa. O EDS exibiu os elementos químicos oxigênio e carbono, característicos do polímero. No DRX observou-se que o PEEK tem comportamento de material semicristalino. Os espectros de FTIR revelaram as bandas típicas de absorção do PEEK. Na análise térmica realizada por calorimetria exploratória diferencial do PEEK, observou-se a presença de um pico endotérmico em 344,68° C, com início em aproximadamente 320° C e final em 349° C. De acordo com os resultados, verifica-se que o PEEK apresenta medidas de ângulo de contato menor que 90°, indicando hidrofilicidade. No ensaio mecânico, percebeu-se que tanto o módulo elástico quanto a resistência à tração do PEEK é mais próximo ao osso que o titânio. Conclui-se que o PEEK apresenta propriedades compatíveis para ser utilizado como biomaterial / In odontology, the dental osseointegrated implants have been the best option for the treatment of total dental loss. These allow a functional and esthetical recovery, such as the ability of chewing. Nowadays, the use of polymers to fabricate osseointegrated implants has been introduced in replacement to the titanium’s conventionals, as for example the polyether ether ketone (PEEK). Therefore, the purpose of this work is to evaluate the properties of polyether ether ketone (PEEK) to use in dental applications, describing it physically, chemically and morphologically, in the use perspective as implant. The samples have been analyzed through a Scanning Transmission Electron Microscope (STEM), Energy Dispersive x-ray Spectroscopy (EDS), X-ray Diffraction, (XRD), Fourier Transform Infrared (FTIR), Differential Scanning Calorimeter (DSC), Wettability by contact Angle. The result of the STEM showed a characteristic of a flat and dense surface material. The EDS displayed the chemical elements oxygen and carbon, typical of a polymer. On the XRD, the PEEK was observed to behave as a semi crystalline material. The spectrums of the FTIR revealed typical bands of PEEK’s absortion. On the thermical analysis by PEEK’s differential scanning calorimeter, it was observed the presence of an endothermic peak in 344,68˚C, initiating approximately with 320˚C and ending in 349˚ C. According to the results, it is verified that the PEEK presents measures of contact angle less that 90˚, indicating hydrophilicity. On the mechanic test, it was perceived that the elastic module and PEEK’s traction resistence is the closest to the bone rather than the titanium. The conclusion therefore is that the PEEK shows compatible properties to be used as a biomaterial.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/1158 |
| Date | 12 July 2018 |
| Creators | SILVEIRA, Geiza Ferreira da. |
| Contributors | NEVES, Gelmires de Araújo., FOOK, Marcus Vinicius Lia., LIMA, Verônica Evangelista de., PINTO, Maria Roberta de Oliveira. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0028 seconds