Programa de Pós-Graduação em Engenharia de Materiais. Rede Temática em Engenharia de Materiais, Pró-Reitoria de Pesquisa e Pós-Graduação, Universidade Federal de Ouro Preto. / Submitted by Marise Leite (marise_mg@yahoo.com.br) on 2016-02-26T12:44:50Z
No. of bitstreams: 2
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
DISSERTAÇÃO_CinéticaOxidaçãoCaracterização.pdf: 1774446 bytes, checksum: e0066dabe4edeab9c94093c543a01049 (MD5) / Approved for entry into archive by Oliveira Flávia (flavia@sisbin.ufop.br) on 2016-04-11T12:49:09Z (GMT) No. of bitstreams: 2
DISSERTAÇÃO_CinéticaOxidaçãoCaracterização.pdf: 1774446 bytes, checksum: e0066dabe4edeab9c94093c543a01049 (MD5)
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Made available in DSpace on 2016-04-11T12:49:09Z (GMT). No. of bitstreams: 2
DISSERTAÇÃO_CinéticaOxidaçãoCaracterização.pdf: 1774446 bytes, checksum: e0066dabe4edeab9c94093c543a01049 (MD5)
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
Previous issue date: 2004 / A formação de carepa durante processos industriais a elevadas temperaturas gera
perdas que levam a um aumento dos custos de produção. A caracterização da carepa formada industrialmente e o estudo da cinética desta reação podem levar a um melhor conhecimento do processo de formação dessa carepa, otimizando o processo de laminação a quente e de
decapagem da ACESITA. Com esse objetivo amostras de dois tipos de aço inoxidável foram oxidadas em um forno tubular na faixa de temperaturas entre 600 - 1200ºC, para avaliar a variação de massa com relação ao tempo e com relação à temperatura de ensaio. Ensaios de
difração de raios X e de espectroscopia Mössbauer caracterizaram quais tipos de óxidos foram formados durante a oxidação e quais as proporções desses óxidos na carepa. Diversos parâmetros, como a energia de ativação para o processo de oxidação, foram avaliados. A variação de massa ocorrida durante a oxidação mostrou-se fortemente dependente com relação
à temperatura e ao tempo, aumentando consideravelmente com o aumento desses dois fatores. O aço SAE 304 mostrou-se mais resistente à oxidação em relação ao SAE 430. As fases cristalinas encontradas foram principalmente a hematita e a magnetita, ou mais precisamente um espinélio no caso do SAE 304, sendo encontradas outras fases nos ensaios com tempos e temperaturas menores. A hematita parece formar-se antes da magnetita
durante a oxidação e à medida que a temperatura aumenta a hematita se transforma em magnetita, lembrando que devemos sempre considerar a redução da temperatura no processo de laminação a quente. A explicação provável para a ausência de óxidos de cromo na maioria
das amostras ensaiadas seria a de que tais óxidos volatilizariam a elevadas temperaturas. ____________________________________________________________________________________ / ABSTRACT: The formation of scaling during industrial processes at high temperatures generates losses that lead to an increase of the production costs. The haracterization of the scaling formed industrially and the study of the kinetics of this reaction can result in a better
knowledge of the process of formation of this scaling, optimizing the hot lamination process of the ACESITA. Thus, samples of two types of stainless steels were oxidized in a tubular furnace in the range of temperatures between 600 and 1200ºC to evaluate the gain of mass with relation to the time and temperature of assay. Experiments of X-ray diffraction and Mössbauer spectroscopy had learned which types of oxides had been formed during the oxidation and the ratios of these oxides in the scaling as well. Several parameters such as the activation energy for the oxidation process, were evaluated. The gain of mass during the
oxidation depends both on the temperature and the time, increasing strongly with the increase of these two factors. Steel SAE 304 revealed to be more resistant to the oxidation in comparison with the SAE 430.
The major crystalline phases were hematite and magnetite, or more precisely a spinel
in the case of SAE 304. Minor constituents were found depending on the times and
temperatures of the experiments. Hematite seems to be formed before magnetite during the oxidation, but as the temperature increases the hematite transforms into magnetite. The probable explanation for the absence of chromium oxide in the majority of the assayed samples is that such oxides are volatilized at high temperatures.
Identifer | oai:union.ndltd.org:IBICT/oai:localhost:123456789/6354 |
Date | January 2004 |
Creators | Carvalho, Carlos Eduardo Reis de |
Contributors | Costa, Geraldo Magela da, Cota, André Barros, Rossi, Edson Hugo |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Source | reponame:Repositório Institucional da UFOP, instname:Universidade Federal de Ouro Preto, instacron:UFOP |
Rights | Open access., info:eu-repo/semantics/openAccess |
Page generated in 0.0016 seconds