This work is focused on oxide scale failure and characteristics created in high temperature – supercritical processes. The presence of high temperature corrosion in supercritical processes is minimalised by selection of the right material. For this work was selected material X10CrMoVNb9-1, where formulas of present oxidation scales are Fe2O3, Fe3O4 and FeCr2O4. Each oxidation scale has its own mechanical properties thus it is important to notice scale arrangement, thickness and geometry. Oxide scale mechanical properties, scale failure mechanisms and oxidation scale growth is evaluated in this work. Tension and pressure oxide scale failure are determined by critical values, which are mentioned in this work. Thanks to these values there was possibility to verify the authenticity of the finite element model. Oxidation scales created in heat exchangers are badly accessible thus it is difficult to observe them or remove them mechanically. Tube finite element model with oxidation scales was created in this work. There are simulations of scales on selected steel in supercritical conditions (pressure 24 MPa, temperature 500 °C). Simulation and analytic results are compared. Failure operative conditions are searched for scale FeCr2O4 until its compleate delamination and separation from metal. Aim of this work is to create an oxidation scale model with a possibility of futher use.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:318721 |
| Date | January 2017 |
| Creators | Audyová, Markéta |
| Contributors | Vejvoda, Stanislav, Lošák, Pavel |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0014 seconds