Thermal barrier coating (TBC) systems are widely used on gas turbine components to provide thermal insulation and oxidation protection. TBCs, incombination with advanced cooling, can enable the gas turbine to operate at significantly higher temperatures even above the melting temperature of the metallic materials. There is a permanent need mainly of environmental reasons to increase the combustion turbine temperature, hence new TBC solutions are needed.By using a liquid feedstock in thermal spraying, new types of TBCs can be produced. Suspension plasma/flame or solution precursor plasma spraying are examples of techniques that can be utilized for liquid feedstock thermal spraying.This approach of using suspension and solution feedstock, which is an alternative to the conventional solid powder feed stock spraying, is gaining increasing research interest, since it has been shown to be capable of producing coatings with superior coating performance.The objective of this research work was to explore relationships between process parameters, coating microstructure, thermal diffusivity and thermal conductivity in liquid feedstock thermal sprayed TBCs. A further aim was to utilize this knowledge to produce a TBC with lower thermal diffusivity and lower thermal conductivity compared to state-of-the-art in industry today, i.e. solid feed stock plasma spraying. Different spraying techniques, suspension high velocity oxy fuel,solution precursor plasma and suspension plasma spraying (with axial and radialfeeding) were explored and compared with solid feedstock plasma spraying.A variety of microstructures, such as highly porous, vertically cracked and columnar, were obtained. It was shown that there are strong relationships between the microstructures and the thermal properties of the coatings.Specifically axial suspension plasma spraying was shown as a very promising technique to produce various microstructures as well as low thermal diffusivity and low thermal conductivity coatings.
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:hv-9061 |
Date | January 2016 |
Creators | Ganvir, Ashish |
Publisher | Högskolan Väst, Avd för tillverkningsprocesser, Trollhättan : University West |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Licentiate thesis, comprehensive summary, info:eu-repo/semantics/masterThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Relation | Licentiate Thesis : University West ; 9 |
Page generated in 0.0019 seconds