Erosion during Brazing in Stainless Steel grade 304

The erosion or dissolution of stainless steel grade 304 as base metal by molten brazing fillermetal was investigated using one nickel and two iron based filler metals. The difference betweentwo iron filler metal is 5 % Manganese content in one of the filler metal. The Wettability of fillermetal is effected by oxidation of base or filler metal for which high vacuum or non reacting gasis used as a furnace atmosphere to reduce the partial pressure of oxygen. The furnace parameterseffecting erosion of base metal was observed e.g. peak temperature and brazing time. The effectof filler mass was also observed. The erosion depth was measured by light optical microscope.All the three filler metal shows different erosion behavior in nitrogen atmosphere compare tohigh vacuum. In high vacuum some of the elements evaporates at brazing temperature whichchanges the properties of filler metal. This change of composition in filler metal was observed byEDX analysis. SEM analysis was used to identify different element rich phases.

Identiferoai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-116688
Date January 2012
Creatorsjahanzeb, Nabeel
PublisherKTH, Materialvetenskap
Source SetsDiVA Archive at Upsalla University
LanguageEnglish
Detected LanguageEnglish
TypeStudent thesis, info:eu-repo/semantics/bachelorThesis, text
Formatapplication/pdf
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0016 seconds