This thesis deals with heat treatment of pearlitic steel beams with using of induction heating. The aim of this heat treatment is to improve mechanical properties of steel beams. In theoretical part are described pearlitic steels and theory of induction heating. In experimental part of this thesis analysis of current state of technology with its results was made. Numerical model describing current state of technology was assembled. Then this model was used to recommend adjustments in current technology of heat treatment, which leads to enlargement of heat treated depth. Experiments with adjusted parameters were executed on heat treating machine. Analysis of microstructure using LM and EM, measurement of hardness and fractographic analysis were done. The result of adjustments is enlargement of heat treated depth about half compared with current technology.
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:319561 |
Date | January 2017 |
Creators | Dyčka, Martin |
Contributors | Foret, Rudolf, Jan, Vít |
Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/masterThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0013 seconds