The investigation in this thesis focuses on the synthesis of cation-ordered perovskite phases by introducing anion vacancies into the structure. Complex cation-ordered phases Ba2YMO5 and Ba3YM2O7.5 (M = Fe, Co) have been synthesized using ceramic or citrate gel methods under flowing argon. Close inspection reveals that the structures are constructed from Y2M2O102 basic units which consist of two YO6 octahedra and two MO4 tetrahedra in a rock-salt type arrangement. In the structure of Ba2YMO5 (M = Fe, Co), the neighbouring Y2M2O102 units are connected with an equivalent one in the yz-plane with YO6 octahedra sharing an apex. In the structure of Ba3YM2O7.5 (M = Fe, Co), the basic units are connected to each other by the M2O7 dimers via a chain of Y – O – M – O – M – O – Y bonds. Complex cation ordering can be achieved by carefully controlling the anion vacancies and selecting the cations with different ionic radii. The anion vacancies present in Ba2YMO5 (M = Fe, Co) (space group P21/n) allow the intercalation of anions like O2- and F- into the lattice. The fluorination of Ba2YCoO5 leads to the formation of a new orthorhombic phase Ba2YCoO5F0.42 (space group Pbnm) in which the inserted fluoride ions are distributed in a disordered manner. In contrast, the topochemical oxidation of Ba2YFeO5 leads to the formation of a new orthorhombic phase Ba2YFeO5.5 (space group Pb21m), in which Fe4+ centres are located in 4-coordinate tetrahedral sites and 5-coordinate pyramidal sites, respectively. The polar structure of Ba2YFeO5.5 is confirmed by the observation of second-harmonic generation activity and pyroelectric behaviour. Ba2YFeO5.5 also exhibits a combination of ferromagnetic and antiferromagnetic behaviours at low temperature. LaCa2Fe2GaO8 adopts a six-layer structure consisting of an OOTLOOTR stacking sequence of layers of (Fe/Ga)O6 octahedra (O) and (Fe/Ga)O4 tetrahedra (T), related to that of the four-layer brownmillerite structure (space group Pbma). The chains of tetrahedra in the structure of LaCa2Fe2GaO8 exhibit a cooperative twisting distortion in which the twisting direction of the chains of tetrahedra alternates in adjacent tetrahedral layers. LaxSr2-xCoGaO5+δ (0.5 < x < 1) adopts brownmillerite structures which consist of octahedral and tetrahedral layers with mixed valence of Co2+/Co3+. The members with x = 0.5, 0.6 and 0.7 adopt structures with I2mb space group symmetry, in which all the tetrahedra twist in the same direction. The members with x = 0.8, 0.9 and 1.0 adopt structures with Imma space group symmetry, in which the chains of the tetrahedra twist in a disordered manner. A change in the Co3+ spin state from high spin (HS) to low spin (LS) is observed as the La/Sr ratio increases. The change of the Co3+ spin state can be rationalized on the basis of internal chemical pressure.
Identifer | oai:union.ndltd.org:bl.uk/oai:ethos.bl.uk:604382 |
Date | January 2013 |
Creators | Luo, Kun |
Contributors | Hayward, Michael |
Publisher | University of Oxford |
Source Sets | Ethos UK |
Detected Language | English |
Type | Electronic Thesis or Dissertation |
Source | http://ora.ox.ac.uk/objects/uuid:f36a3f97-70b1-4ab6-819b-d400341a4558 |
Page generated in 0.0017 seconds