Conselho Nacional de Desenvolvimento CientÃfico e TecnolÃgico / Compostos ferroelÃsticos sÃo caracterizados pela possibilidade de apresentarem dois ou mais estados de deformaÃÃo ou strain espontÃneos devendo haver a possibilidade de permutaÃÃo entre estes estados atravÃs da aplicaÃÃo de um stress mecÃnico. O Pb8O5(VO4)2 pode ser classificado como pertencente a este grupo. Sua estrutura cristalina ainda nÃo à bem definida na literatura por conta de certas adversidades encontradas durante as anÃlises das mesmas, no entanto, fazendo uso de difraÃÃo de raios-X em diversos cristais deste composto discutiremos seus provÃveis grupos pontuais. Sabe-se tambÃm que hà uma relaÃÃo direta entre os estados de strain e as estruturas de domÃnios sob condiÃÃes ambientes de temperatura e pressÃo. Diversas tÃcnicas espectroscÃpicas foram empregadas afim de analisar como a estrutura cristalina destes compostos pode variar de acordo com as dimensÃes de cada cristal. Dessa forma, verificamos a existÃncia de trÃs fases sob condiÃÃes ambiente, bem como a possibilidade de uma transiÃÃo de fase espontÃnea para cristais da ordem de unidades de micrometros quadrados. O comportamento estrutural do Pb8O5(VO4)2 com o aumento de temperatura foi estudado detalhadamente por diversos autores. Eles reportaram a existÃncia de duas transiÃÃes de fase durante o aquecimento, uma transiÃÃo de segunda ordem por volta de 440 K e outra de primeira ordem por volta de 520 K. A transiÃÃo de primeira ordem leva os cristais de Pb8O5(VO4)2 da fase ferroelÃstica para a fase paraelastica. Contudo, uma vez que cristais ferroelÃsticos apresentam mudanÃas de estados de strain espontÃneos atravÃs da aplicaÃÃo de stress mecÃnico, fizemos uso de medidas de espalhamento Raman com aumento de pressÃo hidrostÃtica em amostras de Pb8O5(VO4)2 para acompanhar o comportamento espectral dos mesmos durante estas variaÃÃes de pressÃo. Assim, observamos um fenÃmeno de amorfizaÃÃo da amostra por volta de 11 GPa e obtivemos fortes indÃcios de trÃs transiÃÃes de fase em aproximadamente 1, 3.5 e 6 GPa. / Ferroelastic compounds are characterized by the possibility to present two or more states of spontaneous strain which could be permuted by application of mechanical stress. Pb8O5(VO4)2 can be classified as belonging to this group. Its crystal structure is not well defined in the literature due to certain adversities found during the data analysis. However, making use of X-ray diffraction in several crystals of this compound we will discuss their probable point groups. It is also known that there is a direct relation between the states of strain and the domains pattern at ambient conditions of temperature and pressure. Several spectroscopic techniques were employed in order to analyze how the crystal structure of these compounds varies according to the dimensions of each crystal. Therefore, we observed the existence of three phases under ambient conditions as well as the possibility of a spontaneous phase transition in crystals of order to units of square micrometers. The structural behavior of Pb8O5(VO4)2 with increasing temperature has been studied in detail by different authors. They reported the existence of two phase transitions on heating, one second-order transition at about 440 K and another first-order around 520 K. The first-order phase transition leads the Pb8O5(VO4)2 crystals of ferroelastic phase to paraelastic phase. However, since ferroelastics crystals show changes of state of spontaneous strain through the application of mechanical stress, we made use of Raman scattering measures with increasing of hydrostatic pressure on samples of Pb8O5(VO4)2 to accompany the spectral behavior of the same during these pressure variations. This way we observed a phenomenon of amorphization of the sample around 11 GPa and obtained strong evidences from three phase transitions at approximately 1, 3.5 and 6 GPa.
Identifer | oai:union.ndltd.org:IBICT/oai:www.teses.ufc.br:8522 |
Date | 03 September 2014 |
Creators | Bruno Sousa AraÃjo |
Contributors | Alejandro Pedro Ayala |
Publisher | Universidade Federal do CearÃ, Programa de PÃs-GraduaÃÃo em FÃsica, UFC, BR |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | application/pdf |
Source | reponame:Biblioteca Digital de Teses e Dissertações da UFC, instname:Universidade Federal do Ceará, instacron:UFC |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.002 seconds