The annealing behaviour, including studies of recrystallisation kinetics and development of crystallographic texture, of two low carbon steels after different cold rolling reductions have been investigated using Optical Microscopy (OM), Electron Back-Scatter Diffraction (EBSD) and Transmission Electron Microscopy (TEM). The primary recrystallisation behaviour of 20, 50, 70 and 90% cold rolled Interstitial Free (IF) and High Strength Low Alloy (HSLA) steels was studied. The HSLA was initially processed to give a volume fraction of about 0.2 of fine pearlite colonies, which acted as mechanically hard particles. The presence of such particles on the HSLA steel significantly reduced the temperature needed for recrystallisation by enhancing the recrystallisation and acting as nucleation sites by the Particle Stimulated Nucleation (PSN) mechanism. The inhomogeneous deformation and the local orientation changes introduced in the neighbourhood of the carbide particles (i.e. the particle deformation zone) were observed using TEM and selected area electron diffraction. The JMAK model was used to analyse the recrystallisation kinetics of the two steels. The experimental data plotted according to the JMAK model could be represented by straight lines with a JMAK exponent n falling in the range from 1.4 to 2.0. The development of crystallographic textures after cold rolling reductions and subsequent recrystallisation has been investigated. The texture development is shown to be largely dependent on the rolling reduction. With increasing rolling reduction, the annealing texture show gradual intensification of α- and γ-fibre components. However, the intensity of both fibres is weaker in the HSLA steel. Despite the dominance of PSN in HSLA steel, the recrystallisation textures were similar to that of the rolling textures with weaker intensity of both fibres. To help clarify the reasons for that, in-situ EBSD experiments of recrystallising HSLA steel deformed to 50% and 70% have been carried out. It shows that the formation of the nucleus seems to occur within the deformation zones in regions away from the particle surface leading to recrystallisation textures similar to that of the rolling textures (i.e. both α- and γ-fibre exist). The validity of this assumption has been confirmed by the use of Monte Carlomodelling. This model was used to simulate, in general way, and study the phenomenon of PSN during the recrystallisation process. The simulation shows the discontinuous evolution of the subgrains in the deformation zone to form recrystallisation nuclei around the particle. It shows also the subsequent growth of these nuclei to consume the matrix region around the particle. The simulation results are shown to match with the experimentally observed features of the recrystallisation phenomena in low carbon steel containing coarse cementite particles.
Identifer | oai:union.ndltd.org:bl.uk/oai:ethos.bl.uk:516406 |
Date | January 2010 |
Creators | Almojil, Marwan |
Contributors | Bate, Peter |
Publisher | University of Manchester |
Source Sets | Ethos UK |
Detected Language | English |
Type | Electronic Thesis or Dissertation |
Source | https://www.research.manchester.ac.uk/portal/en/theses/deformation-and-recrystallisation-in-low-carbon-steels(8e972aa3-ac71-4c36-ae48-a804bf555552).html |
Page generated in 0.0845 seconds