A newly developed martensitic stainless steel powder, called “powder A”, designed for surface coating with laser cladding and PTA cladding was characterized. The purpose with powder A is to achieve both good corrosion resistance and wear resistance in a stainless steel grade. The investigation of powder A was divided into cladding characterization, microstructural investigation and a property comparison to existing grades 316 HSi and 431 L. Powder A was successfully deposited with laser cladding, exhibiting a wide process window, and PTA cladding. In both cases no preheating was required and no cracks were formed. The microstructure examination indicates that powder A has a martensitic structure possibly containing small amounts of ferrite in the grain boundaries. Thermodynamic calculations in computer software Thermo-Calc 4.1 supported this theory. The microstructure of powder A proved to be very stable over a wide range of cladding parameters. Powder A was significantly harder than 316 HSi and 431 L and had better corrosion resistance than 431 L in a chloride environment. Powder A had similar corrosion properties as 316 HSi in the experiments made .The wear performance of the powder A coatings was similar to 431 L. This was surprising since the hardness of the powder A coatings is significantly higher compared to 431 L.
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-163788 |
Date | January 2015 |
Creators | Tibblin, Fritjof |
Publisher | KTH, Materialvetenskap |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0017 seconds