Previous issue date: 2014-04-28 / Conselho Nacional de Desenvolvimento Cient?fico e Tecnol?gico / Doped lanthanum chromite ( LaCrO3 ) has been the most common material used as interconnect in solid oxide fuel cells for high temperature ( SOFC-HT ) that enabling the stack of SOFCs. The reduction of the operating temperature, to around 800 ? C, of solid oxide fuel cells enabled the use of metallic interconnects as an alternative to ceramic LaCrO3, From the practical point of view, to be a strong candidate for interconnect the material must have good physical and mechanical properties such as resistance to oxidizing and reducing environments, easy manufacture and appropriate thermo-mechanical properties. Thus, a study on the physic-mechanical interconnects La0,8Sr0,2Cr0,92Co0,08O3 ceramics for SOFC -AT obtained by the method of combustion , as well as thermo-mechanical properties of metallic interconnects (AISI 444) covered with La0,8Ca0,2CrO3 by deposition technique by spray-pyrolysis fuel cells for intermediate temperature (IT-SOFCs). The La0,8Sr0,2Cr0,92Co0,08O3 was characterized by X -ray diffraction(XRD) , density and porosity , Vickers hardness (HV) , the flexural strength at room temperature and 900 ?C and scanning electron microscopy (SEM). The X -ray diffraction confirmed the phase formation and LaCrO3 and CoCr2O4, in order 6 GPa hardness and mechanical strength at room temperature was 62 MPa ceramic Interconnector. The coated metal interconnects La0,8Ca0,2CrO3 passed the identification by XRD after deposition of the film after the oxidation test. The oxidative behavior showed increased resistance to oxidation of the metal substrate covered by La0,8Ca0,2CrO3 In flexural strength of the coated metal substrate, it was noticed only in the increased room temperature. The a SEM analysis proved the formation of Cr2O3 and (Cr,Mn)3O4 layers on metal substrate and confirmed the stability of the ceramic La0,8 Ca0,2CrO3 film after oxidative test / A cromita de lant?nio (LaCrO3) dopada tem sido o material mais utilizado como interconector nas pilhas a combust?vel de ?xido s?lido de alta temperatura(PaCOS-AT), possibilitando o empilhamento(stack) da PaCOS. A redu??o da temperatura de opera??o, em torno de 800 ?C, das pilhas a combust?vel de ?xido s?lido, tornou poss?vel o uso de interconectores met?licos como alternativa aos LaCrO3 cer?micos. Do ponto de vista pr?tico para o material ser forte candidato a interconector deve ter boas propriedades f?sicas e mec?nicas, como resist?ncia a ambientes oxidantes e redutores, f?cil fabrica??o e propriedades termo-mec?nicas adequadas. Por este motivo realizou-se um estudo sobre as propriedades fisico-mec?nicas de interconectores de La0,8Sr0,2Cr0,92Co0,08O3 cer?mico para PaCOS-AT obtido pelo m?todo da combust?o, como tamb?m sobre as propriedades termo-mec?nicas de interconectores met?licos (AISI 444) recobertos com La0,8Ca0,2CrO3 pela t?cnica de deposi??o por spray-pir?lise para Pilhas a combust?vel de temperatura intermediaria (PaCOS-TI). A La0,8Sr0,2Cr0,92Co0,08O3 foi caracterizada por meio de difra??o de raios X (DRX), densidade e porosidade, dureza Vickers (HV), resist?ncia mec?nica a flex?o na temperatura ambiente e a 900?C e microscopia eletr?nica de varredura (MEV). A difra??o de raios X comprovou a forma??o das fases LaCrO3 e CoCr2O4, dureza na ordem de 6 GPa e resist?ncia mec?nica a temperatura ambiente de 62 MPa do interconector cer?mico. A avalia??o das fases formadas no interconector met?lico recoberto com La0,8Ca0,2CrO3 tanto na deposi??o quanto ap?s o ensaio oxidativo foi realizado por DRX. O comportamento oxidativo evidenciou o aumento da resist?ncia a oxida??o do substrato met?lico recoberto por La0,8Ca0,2CrO3. Na resist?ncia mec?nica a flex?o do substrato met?lico recoberto, notou-se o aumento apenas na temperatura ambiente. Com aux?lio do MEV comprovou-se a forma??o das camadas de Cr2O3 e (Cr,Mn)3O4 sobre o substrato met?lico e confirmou-se a estabilidade do filme cer?mico de La0,8Ca0,2CrO3 ap?s o ensaio oxidativo
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/12864 |
| Date | 28 April 2014 |
| Creators | Sousa, Cl?wsio Rog?rio Cruz de |
| Contributors | CPF:50580396720, http://lattes.cnpq.br/5460040602567184, Delmonte, Mauricio Roberto Bomio, CPF:27816279841, http://lattes.cnpq.br/9558299312183852, Silva, Vamberto Monteiro da, CPF:67456863415, Ramalho, Eduardo Galv?o, CPF:03605359418, http://lattes.cnpq.br/3006037569302325, Segadaes, Ana Maria Bastos Costa, http://lattes.cnpq.br/8903008150542337, Acchar, Wilson |
| Publisher | Universidade Federal do Rio Grande do Norte, Programa de P?s-Gradua??o em Ci?ncia e Engenharia de Materiais, UFRN, BR, Processamento de Materiais a partir do P?; Pol?meros e Comp?sitos; Processamento de Materiais a part |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | application/pdf |
| Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0019 seconds