This thesis examines the optical properties of nanoscale silicon and the sensitization of Er with Si. In this context, it predominantly investigates the role of defects in limiting the luminescence of Si nanocrystals, and the removal of these defects by hydrogen passivation. The kinetics of the defect passivation process, for both molecular and atomic hydrogen, are studied in detail. Moreover, the optical absorption of Si nanocrystals and the effect of annealing environment (during nanocrystal synthesis) on the luminescence are investigated. The effect of annealing temperature and hydrogen passivation on the coupling (energy transfer) of Si nanocrystals to optically active centres (Er) is also examined.¶
The electronic structure of silicon-implanted silica slides is investigated through optical absorption measurements. Before and after annealing to form Si nanocrystals, optical absorption spectra from these samples show considerable structure that is characteristic of the particular implant fluence. This structure is shown to correlate with the transmittance of the samples as calculated from the modified refractive index profile for each implant. Due to the high absorption coefficient of Si at short wavelengths, extinction at these wavelengths is found to be dominated by absorption. As such, scattering losses are surprisingly insignificant.
To eliminate interference effects, photothermal deflection spectroscopy is used to obtain data on the band structure of Si in these samples. This data shows little variance from bulk Si
structure and thus little effect of quantum confinement. This is attributed to the dominance of
large nanocrystals in the absorption measurements.¶
The effect of annealing environment on the photoluminescence (PL) from silicon nanocrystals synthesized in fused silica by ion implantation and thermal annealing is studied as a function of annealing temperature and time. Interestingly, the choice of annealing environment (Ar, N2, or 5 % H2 in N2) is found to affect the shape and intensity of luminescence emission
spectra, an effect that is attributed both to variations in nanocrystal size and the density of defect states at the nanocrystal/oxide interface.¶
The passivation kinetics of luminescence-quenching defects, associated with Si nanocrystals in SiO2, during isothermal and isochronal annealing in molecular hydrogen are studied by time-resolved PL. The passivation of these defects is modeled using the Generalized Simple
Thermal model of simultaneous passivation and desorption, proposed by Stesmans. Values for the reaction-rate parameters are determined for the first time and found to be in excellent
agreement with values previously determined for paramagnetic Si dangling-bond defects (Pb type centers) found at planar Si/SiO2 interfaces; supporting the view that non-radiative recombination in Si nanocrystals is dominated by such defects.¶
The passivation kinetics of luminescence-quenching defects during isothermal and isochronal annealing in atomic hydrogen are studied by continuous and time-resolved PL. The kinetics are compared to those for standard passivation in molecular hydrogen and found to be
significantly different. Atomic hydrogen is generated using the alneal process, through reactions between a deposited Al layer and H2O or OH radicals in the SiO2. The passivation and desorption kinetics are shown to be consistent with the existence of two classes of nonradiative defects: one that reacts with both atomic and molecular hydrogen, and the other that reacts only with atomic hydrogen. A model incorporating a Gaussian spread in activation energies is presented that adequately describes the kinetics of atomic hydrogen passivation and dissociation for the samples.¶
The effect of annealing temperature and hydrogen passivation on the excitation cross-section and PL of erbium in silicon-rich silica is studied. Samples are prepared by co-implantation of Si and Er into SiO2 followed by a single thermal anneal at temperatures ranging from 800 to
1100 degrees C, and with or without hydrogen passivation performed at 500 degrees C. Using time-resolved PL, the effective erbium excitation cross-section is shown to increase by a factor of 3, while the number of optically active erbium ions decreases by a factor of 4 with increasing annealing temperature. Hydrogen passivation is shown to increase the luminescence intensity
and to shorten the luminescence lifetime at 1.54 micron only in the presence of Si nanocrystals. The implications of these results for realizing a silicon-based optical amplifier are also discussed.
| Identifer | oai:union.ndltd.org:ADTP/216800 |
| Date | January 2006 |
| Creators | Wilkinson, Andrew Richard, arw109@rsphysse.anu.edu.au |
| Publisher | The Australian National University. Research School of Physical Sciences and Engineering |
| Source Sets | Australiasian Digital Theses Program |
| Language | English |
| Detected Language | English |
| Rights | http://www.anu.edu.au/legal/copyrit.html), Copyright Andrew Richard Wilkinson |
Page generated in 0.0025 seconds