The Ni-base superalloy, IN-718, has been coated with alumina sols. Coated surfaces, carrying alumina layers having thicknesses between 0.6 μm and 3.6 μm show a significantly reduced oxidation rate when compared with uncoated reference surfaces, even if heating temperature is increased up to 900 °C and heating time is extended to 800 h. Alumina layers were prepared via sol-gel processing using a modified Yoldas procedure to obtain alumina sols. No change in rheological sol behavior was observed for more than 1 year of aging under static conditions at room temperature. Depending on pH value, modified Yoldas sols contain a manifold of Al species, among them Al13 polycations. Thermal evolution of sol derived alumina powders depends on Al speciation of parent sols. Depending on sol composition, both gamma-Al2O3 and eta-Al2O3 occur as intermediate transition aluminas. Phase composition and gas phase velocity influence oxygen permeability of thin layers prepared with modified Yoldas sols.
| Identifer | oai:union.ndltd.org:DRESDEN/oai:qucosa:de:qucosa:22583 |
| Date | 08 December 2006 |
| Creators | Dressler, Martin |
| Contributors | Nofz, Marianne, Aneziris, Christos G., Biermann, Horst, TU Bergakademie Freiberg |
| Source Sets | Hochschulschriftenserver (HSSS) der SLUB Dresden |
| Language | English |
| Detected Language | English |
| Type | doc-type:doctoralThesis, info:eu-repo/semantics/doctoralThesis, doc-type:Text |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0021 seconds