Biomaterial surface properties such as microtopography and energy can change cellular responses at the cell-implant interface. Phospholipase D (PLD) is required for differentiation of osteoblast-like MG63 cells on machined and grit-blasted titanium surfaces. Here, we determined if PLD is also required on microstructured/high-energy substrates and the mechanism involved. shRNAs for human PLD1 and PLD2 were used to silence MG63 cells. Wild-type and PLD1 or PLD1/2 silenced cells were cultured on smooth-pretreatment surfaces (PT); grit-blasted, acid-etched surfaces (SLA); and SLA surfaces modified to have higher surface energy (modSLA). PLD was inhibited with ethanol or activated with 24,25-dihydroxyvitamin-D₃ [24R,25(OH)₂D₃]. As surface roughness/energy increased, PLD mRNA and activity increased, cell number decreased, osteocalcin and osteoprotegerin increased, and protein kinase C (PKC) and alkaline phosphatase specific activities increased. Ethanol inhibited PLD and reduced surface effects on these parameters. There was no effect on these parameters after knockdown of PLD1, but PLD1/2 double knockdown had effects comparable to PLD inhibition. 24R,25(OH)₂D₃increased PLD activity and production of osteocalcin and osteoprotegerin, but decreased cell number on the rough/high-energy surfaces. These results confirm that surface roughness/energy-induced PLD activity is required for osteoblast differentiation and that PLD2 is the main isoform involved in this pathway. Here we showed that PLD is activated by 24R,25(OH)₂D₃ in a surface-dependent manner and inhibition of PLD reduced the effects of surface microstructure/energy on PKC, suggesting that PLD mediates the stimulatory effect of microstructured/high-energy surfaces via PKC-dependent signaling.
| Identifer | oai:union.ndltd.org:GATECH/oai:smartech.gatech.edu:1853/26462 |
| Date | 19 November 2008 |
| Creators | Fang, Mimi |
| Publisher | Georgia Institute of Technology |
| Source Sets | Georgia Tech Electronic Thesis and Dissertation Archive |
| Detected Language | English |
| Type | Thesis |
Page generated in 0.0015 seconds