Orientador: Fernando Iikawa / Tese (doutorado) - Universidade Estadual de Campinas, Instituto de Fisica Gleb Wataghin. / Made available in DSpace on 2018-08-12T12:58:46Z (GMT). No. of bitstreams: 1
Gomes_PauloFreitas_D.pdf: 14344200 bytes, checksum: 55a7f7d3b644c0dc43151a411d53757b (MD5)
Previous issue date: 2009 / Resumo: No presente trabalho apresentamos um estudo da luminescência de érbio em nanocristais de silício (nc-Si) e nanofios de óxido de zinco (nw-ZnO). Os nanocristais de silício com érbio são obtidos através do tratamento térmico de filmes finos amorfos de sub-óxidos de silício (SiOx) preparados por rf-sputtering, variando a concentração de Oxigênio e érbio durante o crescimento. O érbio é adicionado aos filmes cobrindo parcialmente a superfície do alvo de silício com pequenos cacos de érbio metálico. Medidas de espectroscopia Raman e microscopia eletrônica de alta resolução (HRTEM) fornecem o tamanho e densidade de nanocristais em cada amostra. Medidas de fotoluminescência (PL) dos nanocristais na temperatura ambiente mostram que o tamanho dos nanocristais varia com a concentração de oxigênio e temperatura de tratamento térmico. A dependência da PL dos nanocristais com a temperatura pode ser entendida considerando a competição entre processos radiativos e não-radiativos. Em amostras com érbio a taxa de recombinação não-radiativa é maior que nas amostras sem érbio. O estudo da PL dos nanocristais e dos íons Er3+ mostra que o Er3+ funciona como um centro de recombinação não-radiativa para a energia proveniente da recombinação de portadores nos nanocristais. Neste caso, parte da energia gerada nos nanocristais é transferida para os íons Er3+ ao invés de ser emitida na forma de fótons. Também é possível observar que a intensidade da PL do Er3+ depende da intensidade da PL dos nanocristais e é maior em amostras contendo nanocristais de ~3nm (que emitem em ~1,5eV), indicando que a transferência é ressonante (com a excitação 4I15/2 ---> 4I9/2 do Er3+ que corresponde a uma energia de 1,5eV).
Os nanofios de ZnO com érbio são preparados por deposição vapor-liquid-solid (VLS) e por electrospinning. Em amostras preparadas por VLS, o érbio é depositado sobre os nanofios após sua preparação. No electrospinning um composto organometálico de érbio é adicionado ao polímero precursor. É observada luminescência de érbio quando as amostras são excitadas com um comprimento de onda ressonante com algum nível mais energético do Er3+. Nanocristais de E2O3 são observados por HRTEM na superfície dos nanofios preparados por VLS. Medidas de EXAFS revelam que a vizinhança do Er nessas amostras é idêntica à do óxido Er2O3, indicando que não ocorreu dopagem substitucional do ZnO. / Abstract: We present a study of erbium luminescence in silicon nanocrystals (nc-Si) and zinc oxide nanowires (nw-ZnO). Silicon nanocrystals are produced by annealing of amorphous sub-oxide thin films (SiOx) prepared by rf-sputtering varying the oxygen and erbium concentration during growth. Erbium is added by partially covering the silicon target surface with small pieces of metallic erbium. Raman spectroscopy and HRTEM measurements reveal the size and density of nanocrystals in each sample. Photoluminescence (PL) measurements at room temperature show that the nanocrystal size changes with oxygen concentration and annealing temperature. The PL dependence on the temperature can be understood considering a competition between radiative and non-radiative processes. In samples with erbium the non-radiative recombination rate is higher than in samples without erbium. The study of the nanocrystal and Er3+ PL show that Er3+ behaves as non-radiative recombination centers for excited carriers in the nanocrystals. Part of the energy from the nanocrystals is transferred to Er3+ instead of being emitted as light. The Er3+ PL intensity depends on the nanocrystal PL intensity and is higher in samples containing nanocrystals ~3nm (which emit at ~1.5eV), indicating that the energy transfer is resonant (with the 4I15/2 -----> 4I9/2 Er3+excitation at ~1.5eV)
ZnO nanowires were prepared by vapor-liquid-solid (VLS) deposition and by electrospinning. In the VLS method erbium is deposited on the nanowires after growth. In the electrospinning method a metallorganic compound is added to the polymer precursor. Erbium PL is observed when the samples are excited by one of the Er3+ higher transitions. Er2O3 nano-crystals are observed by HRTEM on the surface of the nanowires prepared by VLS. EXAFS measurements in these samples show that the Erneighborhood is identical to that of E2O<>3 indicating that there was no substitutional / Doutorado / Física / Doutor em Ciências
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/277734 |
Date | 12 August 2018 |
Creators | Gomes, Paulo Freitas |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Iikawa, Fernando, 1960-, Zanatta, Antonio Ricardo, Meneses, Eliermes Arraes, Marques, Gilmar Eugenio, Antonelli, Alex |
Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Física Gleb Wataghin, Programa de Pós-Graduação em Física |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Format | 146 p. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.1315 seconds