Using photovoltaic effect of Hg lamp on contactless electroreflectance spectroscopy to study transition mechanism of c-plane ZnO

Photo reflectance¡]PR¡^ and Contactless electroreflectance¡]CER¡^spectra of Zn and O-faces of a c-plane ZnO bulk have been measured at room temperature, respectively. It was found that the phase of PR is the same as that of CER for the Zn-face and they are inverted for the O-face. This indicates a polarization induced field existing in the c- plane ZnO bulk due to nonzero spontaneous polarization. In addition, a mercury lamp was focused on the ZnO sample in the CER measurements to provide a photovoltaic voltage to reduce electric field in the sample. The CER spectrum with Hg lamp is more blue-shifted and its amplitude is smaller than that without Hg lamp. Hence, the type of transitions was classified as excitonic transition. The A, B, and C excitonic transition energies were obtained by fitting experimental spectra.

Identiferoai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0705111-125111
Date05 July 2011
CreatorsCheng, An-hao
ContributorsYung-Sung Chen, Dong-Po Wang, Yan-Ten Lu
PublisherNSYSU
Source SetsNSYSU Electronic Thesis and Dissertation Archive
LanguageCholon
Detected LanguageEnglish
Typetext
Formatapplication/pdf
Sourcehttp://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0705111-125111
Rightsnot_available, Copyright information available at source archive

Page generated in 0.0024 seconds