Orientador: Luís Roberto Marcondes Martins / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-27T03:21:27Z (GMT). No. of bitstreams: 1
Santos-Caldeira_MilenaMariaPierre_D.pdf: 2166037 bytes, checksum: 223155da07d2c223b86bb075bcb388de (MD5)
Previous issue date: 2015 / Resumo: Dentro da abordagem minimamente invasiva da doença cárie, um material resinoso a base de metacrilatos, denominado infiltrante Icon® (DMG), foi apresentado com objetivo de paralisar lesões cariosas incipientes em esmalte pela penetração e polimerização dentro das mesmas. Para análise deste material, os objetivos do presente estudo foram: 1) avaliar a influência do pré-aquecimento (AQ) nas propriedades grau de conversão (GC), resistência à flexão (RF), módulo de elasticidade (ME), dureza Knoop (KN) e redução percentual de dureza (RD) de Icon®; e, 2) avaliar a influência do envelhecimento (EN) nas propriedades rugosidade superficial (RS), KN, RF e ME de Icon®. Para avaliação do efeito de AQ (n=10), corpos de prova foram confeccionados (7x2x1mm) de acordo com os grupos divididos em: G1, Icon sem aquecimento; G2, Icon pré aquecido em estufa a 37oC por 1h; G3, Icon com aplicação de ar frio (23oC) por 20 s; G4, Icon com aplicação de ar quente (40oC) por 20 s. GC foi avaliado através da Espectroscopia por Infravermelho Transformada de Fourier (FTIR). RF e ME foram obtidos pelo teste de resistência à flexão de 3 pontos, em máquina de ensaio universal a 0,5mm/min. KN foi avaliada pela média de 3 indentações sob carga de 50g por 15s, e, RD foi avaliada por KN após imersão dos corpos de prova em etanol por 24h. Os dados para avaliação de AQ foram submetidos a ANOVA um critério (5%). Para avaliação de EN (n=20), amostras do infiltrante foram confeccionadas (7x2x1mm) e armazenadas em saliva artificial, a 37oC, até o momento das análises. O fator tempo foi avaliado, nos mesmos espécimes, em 3 níveis (24h, 6 meses e 12 meses) para RS e KN; porém, para RF e ME, tempo foi avaliado em 2 fases (24h e 12 meses) em espécimes distintos devido ao teste destrutivo utilizado. RS foi avaliada, em 24h, 6 e 12 meses, pela média de 3 leituras Ra em rugosímetro. KN foi avaliada em 24h, 6 e 12 meses como previamente descritos para AQ. Enquanto, RF e ME foram avaliados em 24h e 12 meses como também descrito para AQ. Os dados de RS e KN foram submetidos à análise de medidas repetidas e teste de Tukey, enquanto que os dados de RF e ME foram submetidos a ANOVA um critério (5%). O aumento da temperatura do material Icon, não mostrou nenhuma melhora em relação a GC, RF, ME, KN e RD pelos diferentes métodos de preparo testados. Após envelhecimento, RS aumentou significativamente da análise comparado a 6 e 12 meses, enquanto KN sofreu redução nos mesmos 3 tempos testados, havendo correlação inversamente proporcional entre estas propriedades de Icon®. Adicionalmente, houve redução significante de RF e ME após envelhecimento de Icon®. Desta forma, pode-se concluir que o aquecimento do material não interferiu nas propriedades testadas, e o envelhecimento deteriorou as propriedades do infiltrante / Abstract: Within the minimally invasive approach to caries, a methacrylates based material, Icon® infiltrant (DMG), was presented in order to paralyze incipient enamel carious lesions by penetration and polymerization inside caries lesions. For material analysis, the aims of this study were: 1) to evaluate the effect of pre heating material (HE) in conversion degree (CD), flexural strength (FL), elastic modulus (EM), Knoop hardness (KN) and softening ratio (SR); and, 2) to evaluate the effect of artificial aging (AG) in surface roughness (SU), KN, FL and EM. For HE evaluation (n = 10), 10 specimens were prepared (7x2x1mm) according to the groups that were set up as follows: G1, unheated Icon; G2, preheated Icon in oven at 37°C for 1h; G3, Icon with cold air application (23°C) for 20s; G4 Icon with heated air application (40°C) for 20s. CD was measured by Fourier Transform Infrared spectroscopy (FTIR). FL and EM were evaluated by three-point bending test using an universal testing machine by 0,5mm/min. KN was assessed by three indentations average on load of 50g for 15s. And crosslink density was indirectly assessed by hardness softening ratio after ethanol immersion for 24h. The HE evaluation data were submitted to one-way ANOVA (5%). For AG evaluation (n = 20), samples were prepared (7x2x1mm) and stored in artificial saliva at 37°C until the analysis time. The time factor was evaluated in the same specimens, on 3 levels (24h, 6 months and 12 months) for SU and KN; however, for FL and EM, the time was evaluated in 2 levels (24h and 12 months) at different specimens because of the destructive testing. SU was evaluated at 24h, 6 and 12 months, by 3 readings roughness average (Ra cut-off). KN was assessed at 24h, 6 and 12 months, as previously described for AQ. FL and EM were evaluated at 24h and 12 months as well as described for AQ. Data from SU and KN were submitted to repeated measures analysis and Tukey test, while FL and EM data were submitted to one-way ANOVA (5%). Hight temperature did not improved CD, FL, EM, KN and SR by different prepare methods tested. Aging significantly increased SU from the initial analysis compared to 6 and 12 months, while KN decreased in the same three times tested, with inverse correlation between the properties. There was a significant FL and EM reduction after material aging. Therefore, it can be concluded that heating did not affect material properties tested, however, aging deteriorated infiltrant properties / Doutorado / Dentística / Doutora em Clínica Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289727 |
| Date | 24 February 2015 |
| Creators | Santos-Caldeira, Milena Maria Pierre, 1980- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Martins, Luís Roberto Marcondes, 1960-, Baron, Giselle Maria Marchi, Silva, Gisele Rodrigues da, França, Fabiana Mantovani Gomes, Catelan, Anderson, Cavalli, Vanessa |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 61 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.002 seconds