Efeito da distância de fotoativação e meios de imersão sobre a sorção e a solubilidade de um compósito nanoparticulado / Effect of light curing tip distance and immersion media on the sorption and solubility of a nanofilled composite

Orientador: José Roberto Lovadino / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-17T18:06:02Z (GMT). No. of bitstreams: 1
Miranda_DiogodeAzevedo_M.pdf: 1344077 bytes, checksum: 4e28fd76c33592cec253d42d20416b38 (MD5)
Previous issue date: 2011 / Resumo: O objetivo neste estudo foi avaliar o efeito de três distâncias de fotoativação (0mm, 3mm e 6mm) e quatro meios de imersão (saliva artifical, Plax FreshMint, Plax Sem álcool e Plax Whitening) sobre a sorção e solubilidade de um compósito nanoparticulado. Os espécimes foram confeccionados em uma matriz de teflon de 6mm de diâmetro por 1mm de profundidade, e o compósito Filtek¿ Z350 (3M ESPE) foi inserido em incremento único e fotoativado por 20 segundos. Para controlar as distâncias de fotoativação, foi utilizado um dispositivo acoplado a um paquímetro digital. Inicialmente foram confeccionadas 15 amostras (n=5) e, em seguida, realizado o teste de Grau de Conversão (GC%). O GC% dos espécimes foi mensurado antes e após fotoativação, através do espectrômetro de raios infravermelhos transformado de Fourier (FTIR). O GC% foi calculado através da razão entre os espectros não-polimerizados e polimerizados do compósito. Para os testes de sorção e solubilidade foram confeccionados 60 espécimes (n=5), de acordo com as variáveis distâncias de fotoativação e meios de imersão. As amostras foram armazenadas em um dissecador com sílica em gel até a obtenção de uma massa inicial estável (m1). Após estabilização da massa inicial, o diâmetro e a espessura foram aferidos em quatro pontos eqüidistantes utilizando um paquímetro digital e, em seguida, calculado o volume individual (V) de cada amostra. Em seguida, as amostras foram imersas duas vezes ao dia, durante dois minutos nos enxaguatórios por 30 dias. Durante o intervalo de 12 horas, as amostras permaneciam imersas em saliva artificial. Por fim, as amostras foram retiradas das soluções, pesadas (m2) e, em seguida, colocadas no dessecador até a obtenção de uma massa final estável (m3). A sorção (Sp) e solubilidade (SI) foram calculadas através das seguintes fórmulas: Sl = m1-m3/V e Sp= m2-m3/V. Os dados de CG% foram analisados por meio de análise de variância (ANOVA) em esquema de parcelas subdivididas e as comparações múltiplas foram feitas pelo teste de Tukey, considerando o nível de significância de 5%. Os resultados mostraram que independente da distância de fotoativação, a superfície base teve os menores valores de GC% e, que somente quando fotoativado a 6mm de distância, os valores de GC% foram estatisticamente inferiores quando comparados as demais distâncias. Para sorção, os dados foram analisados por ANOVA two way e teste de Tukey, considerando o nível de significância de 5%. Quando fotoativado a 3mm de distância, o Plax Whitening diferiu dos demais enxaguatórios. Durante a fotoativação a 6mm de distância, observou-se diferença estatística em relação as demais distâncias, entretanto não ocorreu diferença estatística entre os enxaguatórios. Os dados de solubilidade foram analisados pelos testes não paramétricos de Kruskal Wallis e Dunn, com nível de significância de 5%. Para todas as distâncias e soluções, os valores foram negativos. Pode-se concluir que o GC% e a sorção do compósito foram influenciados quando fotoativados a 6mm, entretanto, não houve diferença estatística entre os enxaguatórios. Quanto a solubilidade, os valores negativos sugerem que o fenômeno foi mascarado pela sorção / Abstract: The aim of this study was to evaluate the effects of three curing tip distances (0mm, 3mm and 6mm) and four immersion media (artificial saliva, Plax FreshMint, Plax Alcohol-Free and Plax Whitening) on the sorption and solubility of nanofilled composite.The specimens were prepared in a Teflon matrix of 6mm Ø and 1mm height, and Filtek ¿ Z350 (3M ESPE) was inserted in one increment and light cured for 20 seconds. To control the curing tip distances, we used a device coupled to a digital caliper. Initially 15 samples were prepared (n = 5) and then performed the test degree of conversion (DC%). The DC% of the specimens was measured before and after curing, by ray spectrometer, Fourier transform infrared (FTIR). The GC% was calculated as the ratio of the spectra non-polymerized and polymerized composite. For the sorption and solubility tests were prepared 60 specimens (n = 5), according to the variable distances polymerization and immersion media. The samples were stored in a desiccator with silica gel to obtain a stable initial mass (m1). After stabilization of the initial mass, diameter and thickness were measured at four equidistant points by using a digital caliper and then calculated the individual volume (V) of each sample. Then the samples were immersed twice a day for two minutes in mouthrinses for 30 days. During the 12 hours, the samples were immersed in artificial saliva. Finally, samples were taken from the solutions, weighed (m2) and then placed in a desiccator until obtaining a stable final mass (m3). Sorption (Sp) and solubility (SI) were calculated by the following formula: Sl=m1-m3/V and Sp=m3-m2/V. Data from GC% were analyzed by analysis of variance (ANOVA) in split plots and multiple comparisons were made by Tukey test, considering the significance level of 5%. The results showed that regardless of the distance of curing, the bottom surface has the lowest GC%, and that cured only when the distance of 6mm, GC% values were significantly lower when compared with the other distances. For sorption, the data were analyzed by two-way ANOVA and Tukey test, considering the significance level of 5%. When photoactivated to 3mm away, Plax Whitening differed from the others mouthrinses. During polymerization the 6mm away, there was statistical difference from the other distances, but no statistical difference between the mouthrinses. The solubility data were analyzed by nonparametric Kruskal Wallis and Dunn, with a significance level of 5%. For all distances and solutions, the values were negative. It can be concluded that the GC% and sorption properties were influenced when photoactivated to 6mm, however, there was no statistical difference between rinses. As the solubility negative values suggest that the phenomenon was masked by sorption / Mestrado / Dentística / Mestre em Clínica Odontológica

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289478
Date17 August 2018
CreatorsMiranda, Diogo de Azevêdo, 1986-
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Lovadino, José Roberto, 1953-, Filho, Henrique Duque de Miranda Chaves, Aguiar, Flávio Henrique Baggio
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Format49 f. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0033 seconds