Orientador: Simonides Consani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-22T23:08:08Z (GMT). No. of bitstreams: 1
Lancellotti_AillaCarlaRochaAcosta_D.pdf: 3411758 bytes, checksum: b6fff153b65b96dc346dc3df5c29d935 (MD5)
Previous issue date: 2013 / Resumo: O objetivo neste estudo foi avaliar a influência de um sal de iodônio (hexafluorfosfato de difeniliodonio - DFI) nas propriedades de compósitos experimentais para cimentação, quando comparado ao comercial Variolink II, com ativação dupla ou apenas fotoativado por meio de dois aparelhos (Radii-Cal e Bluephase) com emissão de luz em diferentes comprimentos de onda. Ao composto base formado pelos monômeros Bis-GMA e TEGDMA, na proporção de 1:1 mol%, foi acrescido 0,5 mol% de DFI e o controle foi considerado sem DFI, configurando, assim, as duas formulações do agente cimentante resinoso experimental. O sistema fotoiniciador foi composto por 1 mol% de Canforoquinona e 2 mol% de DMAEMA e, como inibidor, 0,1 mol% de BHT. Ao final, foram acrescidas partículas de vidro de bário-alumínio-silicato pré-silanizadas, 60% em peso, como carga inorgânica. Foram realizados os ensaios de densidade de ligação cruzada obtida, indiretamente, através do ensaio de dureza Knoop, resistência à flexão de três pontos e módulo de elasticidade sem ou com fadiga (100.000 ciclos mecânicos e 2.000 ciclos térmicos). Todos os dados foram estatisticamente analisados. A presença de DFI influenciou de forma positiva na dureza Knoop do agente cimentante resinoso experimental quando comparado ao experimental sem DFI. A densidade de ligação cruzada do agente cimentante com 0,5mol% de DFI foi similar a do Variolink II dual. Os valores de resistência à flexão dos cimentos experimentais foram menores que os valores apresentados pelo Variolink II. Os aparelhos de fotoativação tiveram desempenho similar, independente dos agentes cimentantes testados. Concluiu-se que o DFI melhorou algumas das propriedades estudadas; porém, sem alcançar os níveis de propriedades do compósito para cimentação comercial de ativação dupla / Abstract: The aim of this study was to evaluate the influence of incorporating a iodonium salt (diphenyliodonium hexafluorophosphate - DPI) in properties of a experimental resin cement, comparing to the commercial resin cement Variolink II, using either as dual or only photoactivated mode by two light curing units (LCUs) with light emission at different wavelengths, Radii-Cal and Bluephase. A base compound of the monomers Bis-GMA and TEGDMA 1:1 molar ratio was obtained and DPI added at 0 (control) or 0.5 mol%, thus configuring the two experimental formulations resin cement. The photoinitiator system comprised 1 mol% camphorquinone and 2 mol% DMAEMA, and even 0.1 mol% BHT as inhibitor. Finally, was added barium-aluminum-silicate glass, pre silanized 60% mass fraction, as inorganic filler. The crosslinking density, obtained indirectly by testing Knoop hardness, flexural strength and three-point modulus of elasticity in the presence or absence of fatigue (100,000 cycles mechanical and thermal cycles 2000) were assessed. All data were statistically analyzed. The DPI had positively influenced the Knoop hardness when compared to experimental without DPI. The values of flexural strength of experimental cements were lower than the values found by Variolink II. The crosslinking density of cement with 0.5% DPI was similar to dual Variolink II. The LCUs had similar performance in tested cements. It was concluded that the DPI showed a slight improvement in the properties tested, but still not comparing to commercial dual resin cement / Doutorado / Materiais Dentarios / Doutora em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/290056 |
| Date | 22 August 2018 |
| Creators | Lancellotti, Ailla Carla Rocha Acosta, 1982- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Consani, Simonides, 1939-, Macedo, Vanessa Cruz, Mario, Alexandre Luis Souto Borges, Sinhoreti, Mário Alexandre Coelho, Aguiar, Flávio Henrique Baggio |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 38 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0028 seconds