An experimental investigation on the furnace and CO₂ laser densification of sol-gel derived SiO₂-TiO₂-Al₂O₃ planar optical waveguides was performed. Solutions containing equal mole fractions of tetraethoxysiline [Si(C₂H₅O)₄], titanium ethoxide [Ti(C₂H₅O)₄], aluminum tri-sec-butoxide [Al(C₄H₉O)₃] were used to spin films with a nominal 2:2:1 molar SiO₂-TiO₂-Al₂O₃ composition. Emphasis was placed on determining what effects the densification techniques had on film shrinkage, index change, crystallization and composition. Film shrinkage and refractive index change were found to be similar for both densification techniques. Fully dense, amorphous film were obtained with both methods. After densification, further heating caused titania crystalline phases to form with both processing techniques. However, anatase formed in the furnace fired films while rutile formed in the laser irradiated films.
Identifer | oai:union.ndltd.org:arizona.edu/oai:arizona.openrepository.com:10150/291388 |
Date | January 1994 |
Creators | LoStracco, Gregory, 1960- |
Contributors | Fabes, Brian D., Zelinski, Brian J. J. |
Publisher | The University of Arizona. |
Source Sets | University of Arizona |
Language | en_US |
Detected Language | English |
Type | text, Thesis-Reproduction (electronic) |
Rights | Copyright © is held by the author. Digital access to this material is made possible by the University Libraries, University of Arizona. Further transmission, reproduction or presentation (such as public display or performance) of protected items is prohibited except with permission of the author. |
Page generated in 0.0019 seconds