In this thesis, we performed a detailed study of the thermal conductivity in a wide range of quasicrystals. Three systems were studied: AlPdMn, AlCuFe and AlPdRe, and the samples were in both single and polycrystalline form. A further variable was added by introducing a controlled level of defects. / At low temperatures (below 20K), the thermal conductivity is defect limited, being controlled by boundary scattering, two level systems, stacking faults and dislocations. At high temperatures (above 20K), we find the thermal conductivity is limited by intrinsic properties of the quasicrystalline structure and phonon-phonon scattering. / From fitting the thermal conductivity to a detailed model we are able to predict the maximum thermal conductivity of a perfect quasicrystal.
Identifer | oai:union.ndltd.org:LACETR/oai:collectionscanada.gc.ca:QMM.36034 |
Date | January 1999 |
Creators | Legault, Stéphane. |
Contributors | Strom-Olsen, John (advisor) |
Publisher | McGill University |
Source Sets | Library and Archives Canada ETDs Repository / Centre d'archives des thèses électroniques de Bibliothèque et Archives Canada |
Language | English |
Detected Language | English |
Type | Electronic Thesis or Dissertation |
Format | application/pdf |
Coverage | Doctor of Philosophy (Department of Physics.) |
Rights | All items in eScholarship@McGill are protected by copyright with all rights reserved unless otherwise indicated. |
Relation | alephsysno: 001737897, proquestno: NQ55355, Theses scanned by UMI/ProQuest. |
Page generated in 0.0012 seconds