Graphene on SiC has been exposed to thermally cracked hydrogen in an HV environment. Methylene groups ($CH_2$) were observed by IR spectroscopy at a density one hundred times that of lone C-H. Graphene on SiC was also studied using magnetotransport. Weak localization was observed in accordance with theory and scattering times were measured. Exfoliated graphene was prepared on oxide surfaces for controlled gas exposure experiments with graphene FETs. The impact of substrate hydrophobicity on charge transfer with adsorbates was quantitatively measured. Graphene FETs were also produced from graphene grown on copper by chemical vapor deposition and weak localisation measurements were performed. This work is an important step towards the transformation of graphene to graphane by hydrogenation and quantifying the effect of hydrogenation on electronic properties. / Du graphene sur SiC a té exposé a de l'hydrogène craqué sous chauffage. Des groupes de Methylenes ($CH_2$) on été observés par spectroscopie IR ayant une densité cent fois plus grande que les simples groupes C-H. La localisation faible du graphene sur SiC a été observée avec sucès et des temps de diffusion ont été mesuré en accord avec les prédictions théoriques. Du graphene exfolié mécaniquement a été préparé sur de l'oxide afin de mesuré l'effet des gas sur le graphene dans une atmosphère controlée. L'importance d'un substrat hydrophobe sur le transfert de charge avec les espèces adsorbées a été mesuré quantitativement. Des FETs de graphene ont également été produites par croissance sur substrat de cuivre et des mesures de localisation faible ont été prises. Ceci représente un pas important vers la transformation du graphene au graphane en hydrogénant et en quantifiant l'effet de l'hydrogénation sur les propriétés électriques.
| Identifer | oai:union.ndltd.org:LACETR/oai:collectionscanada.gc.ca:QMM.97046 |
| Date | January 2011 |
| Creators | Guillemette, Jonathan |
| Contributors | Thomas Szkopek (Internal/Supervisor) |
| Publisher | McGill University |
| Source Sets | Library and Archives Canada ETDs Repository / Centre d'archives des thèses électroniques de Bibliothèque et Archives Canada |
| Language | English |
| Detected Language | French |
| Type | Electronic Thesis or Dissertation |
| Format | application/pdf |
| Coverage | Master of Science (Department of Physics) |
| Rights | All items in eScholarship@McGill are protected by copyright with all rights reserved unless otherwise indicated. |
| Relation | Electronically-submitted theses. |
Page generated in 0.0216 seconds