Near field recording on high coercivity FePt intermetallic compound media using a high Bsat write element was investigated. Untextured FePt media were prepared by magnetron sputtering on ZrO2 disks at a substrate temperature of 450°C, with post annealing at 450°C for 8 hrs. Both multilayer and cosputtered precursors produced the ordered tetragonal L10 phase with high coercivity between 5kOe and 12kOe. To improve readback noise decrease magnetic domain size, FePtB media were subsequently prepared by cosputtering. Over-write, roll-off, signal to noise ratio and non-linear transition shift (NLTS) ere measured by both metal in gap (MIG) and merged MR heads. FePtB media showed similar NLTS to commercial CoCrPtTa longitudinal media, but 5dB lower signal to noise ratio. By operating recording transducers in near contact, reasonable values of (>30dB) could be obtained.
VSM Rotational Transverse Magnetization has been used for measuring the anisotropy field of magnetic thin films. Magnetization reversal during rotation of a 2D isotropic an applied field is discussed. The relationship between the transverse magnetization My and the applied field H was numerically solved. An excellent approximation for the transverse magnetization is found to be: My/Ms=A1-H/Hk 2.5, where A = 1.1434, and Hk is the anisotropy field. For curve fitting to experimental data, both A and Hk were used as fitting parameters. Comparison between a constructed torque hysteresis method and this VSM RTM method have been made theoretically and experimentally. Both results showed that VSM RTM will give better extrapolation of the anisotropy field. The torque measurement will slightly overestimate the anisotropy field.
The anisotropy fields of FePt and FePtX (X = B, Ni) films were characterized using this VSM RTM technique with comparison to a CoCrTaPt disk. Anisotropy energy was derived. Hc/Hk was used as an indicator for coherent rotation of a single domain. Interactions between magnetic domains were characterized by Kelly-Henkel plot and interactive field factor (IFF). Correlation between coercive force and magnetic anisotropy of grains and the degree of magnetic isolation among grains were discussed. B and Ni were used as diluting agents to the FePt system to decrease saturation magnetization, coercivity, anisotropy field and anisotropy energy. They also decrease the magnetic coupling between neighboring domains, and promote coherent rotation inside each domain.
Identifer | oai:union.ndltd.org:RICE/oai:scholarship.rice.edu:1911/19412 |
Date | January 1999 |
Creators | Li, Ning |
Contributors | Lairson, Bruce M. |
Source Sets | Rice University |
Language | English |
Detected Language | English |
Type | Thesis, Text |
Format | 99 p., application/pdf |
Page generated in 0.7139 seconds