The structural and magnetic properties of Diamagnetic/Ferromagnetic: Cu/Fe multilayers, prepared by DC-magnetron sputtering, were studied as a function of Fe layer thickness tFe. Structural characterization reveals the successful growth of high-quality layered structures along the film growth direction. However, the increasing contribution of the interface roughness was visible with decreasing tFe . X-ray diffraction data indicate the dissolution of Fe atoms in fcc Cu medium due to interfacial mixing. / The magnetic transition from ferromagnetism to paramagnetism with decreasing tFe was confirmed by conversion-electron Mossbauer spectroscopy (CEMS), vibrating sample magnetometry, and magnetotransport measurements. The monotonic decrease in the average hyperfine field with t Fe indicates that the transition is a gradual process as t Fe decreases from 34 A down to 7 A. The isomer shift of the singlets in the CEM spectra suggests the presence of fcc Fe, while the observed doublet is assigned to the Cu-Fe alloy phase at the interfaces. / The variation of magnetoresistance (MR) with t Cu indicates that for a nominal t Fe of 20 A the multilayer has a well-defined superlattice structure, whereas multilayers with nominal tFe, of 5 A have a granular-alloy-like structure. AC susceptometry provided direct evidence for island formation for nominal tFe = 5 A by exhibiting the blocking characteristics of superparamagnets. The temperature-dependence of the magnetization suggests that for nominal tFe = 5 A, 75% of the Fe atoms are in the superparamagnetic bcc phase, leaving the remaining 25% in the Cu-Fe alloy and fcc Fe phases. / The observed magnetic transition is likely due to superparamagnetic relaxation rather than a structural transition from bcc Fe to fcc Fe as t Fe decreases below a critical thickness tC at which a multilayer structure becomes an island structure.
Identifer | oai:union.ndltd.org:LACETR/oai:collectionscanada.gc.ca:QMM.20264 |
Date | January 1997 |
Creators | Lee, Dok Won. |
Contributors | Altounian, Z. (advisor) |
Publisher | McGill University |
Source Sets | Library and Archives Canada ETDs Repository / Centre d'archives des thèses électroniques de Bibliothèque et Archives Canada |
Language | English |
Detected Language | English |
Type | Electronic Thesis or Dissertation |
Format | application/pdf |
Coverage | Master of Science (Department of Physics.) |
Rights | All items in eScholarship@McGill are protected by copyright with all rights reserved unless otherwise indicated. |
Relation | alephsysno: 001609541, proquestno: MQ44203, Theses scanned by UMI/ProQuest. |
Page generated in 0.0018 seconds