Studies on Sintering Silicon Carbide-Nanostructured Ferritic Alloy Composites for Nuclear Applications

Nanostructured ferritic alloy and silicon carbide composite materials (NFA-SiC) were sintered with spark plasma sintering (SPS) method and systematically investigated through X-ray diffraction (XRD), scanning electron microscopy (SEM), as well as density and Vickers hardness tests. Pure NFA, pure SiC, and their composites NFA-SiC with different compositions (2.5 vol% NFA-97.5 vol% SiC, 5 vol% NFA-95 vol% SiC, 97.5 vol% NFA-2.5 vol% SiC, and 95 vol% NFA-5 vol% SiC) were successfully sintered through SPS.

In the high-NFA samples, pure NFA and NFA-SiC, minor gamma-Fe phase formation from the main alfa-Fe matrix occurred in pure NFA 950 degree C and 1000 degree C. The densities of the pure NFA and NFA-SiC composites increased with sintering temperature but decreased with SiC content. The Vickers hardness of the pure NFA and NFA-SiC composites was related to density and phase composition. In the high-SiC samples, NFA addition of 2.5 vol% can achieve full densification for the NFA-SiC samples at relative low temperatures. With the increase in sintering temperature, the Vickers hardness of the pure SiC and NFA-SiC composite samples were enhanced. However, the NFA-SiC composites had relative lower hardness than the pure SiC samples. A carbon layer was introduced in the NFA particles to prevent the reaction between NFA and SiC. Results indicated that the carbon layer was effective up to 1050 degree C sintering temperature. Green samples of gradient-structured NFA-SiC composites were successfully fabricated through slip casting of an NFA-SiC co-suspension. / Master of Science

Identiferoai:union.ndltd.org:VTETD/oai:vtechworks.lib.vt.edu:10919/81763
Date22 July 2016
CreatorsHu, Zhihao
ContributorsMaterials Science and Engineering, Lu, Peizhen, Clark, David E., Aning, Alexander O.
PublisherVirginia Tech
Source SetsVirginia Tech Theses and Dissertation
Detected LanguageEnglish
TypeThesis
FormatETD, application/pdf
RightsIn Copyright, http://rightsstatements.org/vocab/InC/1.0/

Page generated in 0.0015 seconds