Orientador: Roberto Herminio Moretti / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia de Alimentos / Made available in DSpace on 2018-08-03T18:03:59Z (GMT). No. of bitstreams: 1
Arruda_AnaFlaviaPedrosode_M.pdf: 5724087 bytes, checksum: 5f150b453b4e7cefbf71614d42b7f60e (MD5)
Previous issue date: 2003 / Resumo: No presente trabalho, foi estudada a viabilidade do uso da garrafa PET termorresistente como embalagem para néctar de manga, através de ensaios de vida de prateleira comparativos com embalagem cartonada Tetra Brik Aseptic e lata de alumínio comercializadas atualmente, durante um período de 180 dias, com armazenamento sob temperatura ambiente. Néctar de manga comercializado em embalagem cartonada Tetra Brik Aseptic foi adicionado de ácido ascórbico e goma xantana e processado em um sistema composto por um tanque de alimentação com capacidade de 8l, dotado de pressurizador manual para transporte do fluido, e serpentina imersa em banho de água quente, para envase manual realizado à quente (75 OC) em garrafas PET termorresistentes, que foram fechadas e invertidas, e assim mantidas por 2 minutos, antes do resfriamento em água fria. Foi adotado o Planejamento Experimental Completo tipo 22 cujas variáveis independentes foram a concentração do ácido ascórbico (com adições de 14,75 à 85,25 mg/100ml) e goma xantana (com adições de 0,012 à 0,068%), com a finalidade de retardar a oxidação e obter uma viscosidade aceitável pelo consumidor. As análises foram efetuadas com uma freqüência de 45 dias (1 Q, 45Q, 90Q, 135Q e 180Q dia após o processamento). As respostas analisadas foram: ºBrix, acidez titulável, pH, viscosidade, b-carotenos, análises microbiológicas (contagem de bolores/leveduras, contagem total, termófilos e coliformes fecais), determinações do teor de Vitamina C e de Cor e avaliação sensorial. As análises de variância dos resultados indicaram que as condições de processo reais estudadas não influenciaram as características físico-químicas do néctar (ºBrix, acidez titulável, pH e viscosidade). Sob o aspecto microbiológico, foi verificada a eficiência do processo de pasteurização. Durante o período de armazenamento avaliado (180 dias), foi verificado que o produto com teores maiores que 50,0 mg/100mL de ácido ascórbico e teores intermediários de goma xantana (0,04%) resultou em maior aceitabilidade. Sensorialmente, os produtos apresentaram médias de aceitação próximas ou superiores a 7,0, para o atributo de aceitação global, situado na escala hedônica não estruturada, equivalente a "gostei muito" e "gostei moderadamente". Em relação à resposta de cor, até 90 dias, houve redução da Luminosidade (L) para todas as amostras e todos os tratamentos dos produtos em PET ficaram com valores de L próximos aos dos produtos em Tetra Brik Aseptic e lata, e depois deste período a L aumentou para estes produtos e manteve-se relativamente estável nos experimentos com garrafas de PET. Para a cromaticidade (a e b) o produto na lata de alumínio apresentou-se mais escuro, quando comparado com os demais, enquanto as amostras em PET contendo maiores teores de ácido ascórbico adicionados apresentaram menor escurecimento no decorrer do período analisado / Abstract: In this work the viability of using thermoresistant PET bottles as package for mango nectar was studied. Three types of packages were studied: aluminum cans, multifoil package (Tetra Brik Aseptic) and PET bottles, by following the shelf-life of the mango nectar, for 180 days shelf-life period, under room temperature. Commercial mango nectar in multifoil package was used for the experiment. There was added ascorbic acid and xantham gum according to the Experimental Design (Surface Response). Product was thermal treated by heating at 75OC and filled at this temperature in PET bottles, closed and kept for two minutes, before cooling at room temperature. It was used the Complete Experimental Design 22, varying the ascorbic acid (14,75 mg/100mL up to 85,25 mg/100mL) and xantham gum (0,012% up to 0,068%), with the objective of reduce oxidation and get a better viscosity. Determination of: ºBrix, pH, titrable acidity, viscosity, b-carotenes, ascorbic acid, color, sensory evaluation and microbial analysis (molds and yeasts, total count, themophylos and coliforms) were done with a frequency of 45 days (1 Q, 45Q, 90Q, 135Q e 180Q day after bottling). Analysis of Variance showed that the process condition did not influence significantly the nectar physico-chemical characteristics (ºBrix, pH, titrable acidity and viscosity). Under the microbiological aspect, it was concluded the efficiency of the pasteurization process. Under the studied shelf-life period of 180 days, it was observed that mango nectar with higher concentrations of ascorbic acid (over 50mg/1OOmL) and intermediary concentrations (0,04%) of xantham gum, resulted in better acceptability. Organoleptically the products were accepted with scores of 7 or higher, for the attribute "global acceptance", in the non-structured hedonic scale, equivalent to "accept very much". In relation to the color attribute up to 90 days, Luminosity (L) for all samples in all experiments of PET packaged nectar, the L values were very close to the products in multifoil package and Aluminum can, after 90 days L increased for all products and was kept stable when packed in PET. For the chromaticity a and b the canned product in aluminum can presented darker products, when compared to the other experiments. Experiments in PET bottled nectar with higher ascorbic acid content resulted clearer products than the ones with lower addition of ascorbic acid, during the shelf-life period / Mestrado / Tecnologia de Alimentos / Mestre em Tecnologia de Alimentos
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/255539 |
| Date | 16 December 2003 |
| Creators | Arruda, Ana Flavia Pedroso de |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Moretti, Roberto Hermínio, 1940-, Cardello, Helena Maria Andre Bolini, Coltro, Leda, Garcia, Nelson Horacio Pezoa |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia de Alimentos, Programa de Pós-Graduação em Tecnologia de Alimentos |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 93 p., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0026 seconds