Light intensity distribution studies in the heterogeneous photocatalytic reactors were carried out successfully with potassium ferrioxalate chemical actinometry, reproducible light intensity estimates of the irradiation source were obtained. The increased light intensity in the reactor system increased the absorption as determined by actinometry. It was found that reflectivity was a dependent variable but mesh opening area was an independent variable. The photocatalytic mineralization of dichoroacetic acid DCAA, in the presence of TiO2 immobilized on a plate in an externally irradiated bubble column photoreactor had been investigated. The mass transfer and activity evaluation were measured. It was found that increasing the catalyst thickness, increased the photoactivity until it reaches the optimum loading, further loading increase caused the reaction rate to remain constant. This phenomenon was observed with increased lamp power (intensity) and initial solute concentration. However, the catalyst activity was not influenced by the increasing concentration of dissolved oxygen. The reaction rate for DCAA photomineralization was expressed using the Langmuir-Hinsheldwood model.
Identifer | oai:union.ndltd.org:ADTP/234067 |
Date | January 2007 |
Creators | Lee, Ivy Ai Ling, Chemical Sciences & Engineering, Faculty of Engineering, UNSW |
Source Sets | Australiasian Digital Theses Program |
Language | English |
Detected Language | English |
Rights | http://unsworks.unsw.edu.au/copyright, http://unsworks.unsw.edu.au/copyright |
Page generated in 0.0015 seconds