The Mg-modified lead titanate [(Pb1-xMgx)TiO3,abbreviated to PMT] thin films were deposited on Pt/SiO2/Si substrates by spin coating with sol-gel processing in this thesis. 1,3 propanediol was used as solvent to minimize the number of cycles of spin coating and drying processes to obtain the desired thickness of thin film. By changing the Mg content (0~10 mol%) and the heating temperature (500~800¢J), the effects of various processing parameters on the thin films growth are studied. The effects of various Mg contents on the response of pyroelectric IR detector devices are studied also.
Experimental results reveal that the Mg contents will influence strongly on grain size, dielectricity, ferroelectricity and pyroelectricity of PMT thin films. With the increase of Mg content, the grain size of PMT thin film decrease slightly, and the lattice structure of PMT thin film will change from tetragonal to cubic when the Mg content over 8 mole%. The relative dielectric constant of PMT thin film increases from 25 up to 91. The tan
| Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0616100-140320 |
| Date | 16 June 2000 |
| Creators | Kao, Ming-Cheng |
| Contributors | Ying-Chung Chen |
| Publisher | NSYSU |
| Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
| Language | Cholon |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0616100-140320 |
| Rights | unrestricted, Copyright information available at source archive |
Page generated in 0.0023 seconds