Orientadores: Lucia Helena Innocentini Mei, Selma Matheus Loureiro Guedes / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Quimica / Made available in DSpace on 2018-07-23T02:29:26Z (GMT). No. of bitstreams: 1
Pezzin_AnaPaulaTesta_M.pdf: 4716159 bytes, checksum: 2548662a9e88ca376a38d1ecfdb6dc24 (MD5)
Previous issue date: 1997 / Resumo: Recentemente foi desenvolvido na FEQ/UNICAMP um simulador de tecidos (¿bolus¿) à base de PVC/DOP com a finalidade de superficializar a dose máxima nos tratamentos de câncer de pele e de mama. Desta forma, os tecidos sadios próximos ao tumor são protegidos. Este bolus é constituído de 23% de poli(cloreto de vinila) (PVC), 76% de ftalato de dioctila (DOP), além de 1% de outros aditivos. Pesquisas realizadas junto ao Centro de Atenção Integral à Saúde da Mulher (CAISM) do Hospital de Clínicas da UNICAMP, têm mostrado que esse material se comporta como tecido equivalente da pele. Neste trabalho, as amostras deste material foram irradiadas com raios gama e com feixe de elétrons, com doses de 0 a 75kGy e, posteriormente, foi estudado o efeito da radiação ionizante na estrutura molecular e nas propriedades óticas. O amarelecimento foi quantificado por índice de amarelecimento e espectroscopia uv-visível. As alterações estruturais foram caracterizadas por FT-IR, espectroscopia de massas e RMN de 'C ANTPOT. 13¿. A formação de radicais livres foi investigada por RPE. Os resultados obtidos mostraram que a radiação ionizante provoca a formação de grupos cromóforos, tornando visível o amarelecimento a partir de 50kGy (feixes de elétrons) ou de 75kGy (raios gama); promove a eliminação da carbonila, através da cisão radiolítica do DOP, que é mais acentuada quando a radiação é feixe de elétrons; induz uma formação de polienos conjugados provenientes da desidrocloração do PVC e, promove a formação de radicais como conseqüência da cisão homolítica de ligações químicas, tanto do DOP como do PVC... Observação: O resumo, na íntegra, poderá ser visualizado no texto completo da tese digital / Abstract: Recently a tissue simulator called ¿bolus¿ was developed at FEQ/UNICAMP, which is made of dioctyl phtalate and poly (vinyl chloride) (PVC/DOP). This bolus has the function of displacing the maximum dose to the skin and breast cancer. In this way the healthy tissues around the tumor are protected. The bolus composition is 23% (w/w) PVC and 76% (w/w) DOP with 1% (w/w) additives. Research at the Center for Women¿s Health (CAISM) of the Clinical Hospital of UNICAMP has shown that this material can be used as the tissue-equivalent of skin. In the present work, samples of this material were irradiated using both an electron beam and gamma rays at doses in the range of 0 to 75kGy. After irradiation the ionizing radiation effect on the molecular structure and the optical properties were studied. Changes in color were quantified by the yellowness index and diffusion reflectance spectroscopy. Structural changes were studied by Fourier transform infrared, mass spectroscopy and 'C ANTPOT. 13¿ nuclear magnetic resonance. The radicals formed were investigated by electron paramagnetic resonance. The results obtained show that the ionizing radiation promotes the formation of chromophoric groups, easily perceptible at 50kGy (electron beam) or at 75kGy (gamma rays); promotes the elimination of carbonyl groups from DOP radiolytic scission, which is more severe when the radiation is the electron beam, induces the formation of a small amount of conjugated polyenes as a result of PVC dehydrochlorination as well as radical formation as a consequence of the hemolytic scission of the chemical bonds of both DOP and PVC... Note: The complete abstract is available with the full electronic digital thesis or dissertations / Mestrado / Ciencia e Tecnologia de Materiais / Mestre em Engenharia Química
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/267352 |
Date | 27 February 1997 |
Creators | Pezzin, Ana Paula Testa |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Guedes, Selma Matheus Loureiro, Mei, Lúcia Helena Innocentini, 1953-, Agnelli, José Augusto Marcondes, Yoshida, Inez Valéria Pagotto |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Química, Programa de Pós-Graduação em Engenharia Química |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | 119f. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0019 seconds