Corrosion of all aluminum microchannel heat exchangers present a challenge in automotive and heating, ventilation, and air conditioning (HVAC) industries. Reproducibility of Salt Water Acetic Acid Test (SWAAT) has been questioned and a need to new corrosion tests with better reproducibility has risen. Cyclic polarization, that is an electrochemical test, was explored for its suitability for the assessment of AA 3102 tube material that is currently a popular aluminum alloy used in manufacturing of heat exchanger.
Corrosive electrolytes containing 3.5 % sodium chloride with 0.5 % ammonium sulfate (high chloride) or 0.5 % sodium chloride with 3.5 % ammonium sulfate (high sulfate) at their pH or acidic (pH=4) were used to measure corrosion potential (Ecorr), protection potential (Epp), pitting potential (Epit), Tafel constants (βa and βc), corrosion rate (mpy). Corrosive electrolyte used in SWAAT test (4.2% Sea Salt at pH 2.9) was also used to compare corrosion resistance of AA 3102 in SWAAT electrolyte compared to the other electrolytes used in this research. Scanning electron microscopy (SEM) was used to observe and document sample surface corrosion damage after each electrochemical test on all samples.
Results of the cyclic polarization tests indicated that SWAAT electrolytes was the most aggressive electrolyte resulting in highest corrosion rates compared to all other electrolytes used in this investigation. SEM results indicated AA 3102 alloy exhibited higher pitting tendency in electrolytes with high sodium chloride whereas high sulfate electrolytes cause appearance of uniform corrosion surface damage on this alloy. Both high sulfate and SWAAT electrolytes showed intergranular corrosion but high chloride electrolyte showed severe pitting of AA 3102.
Mohammad Navid Dorreyatim- Cyclic Polarization of AA 3102 in Corrosive Electrolytes Containing Sodium Chloride and Ammonium Sulfate. Master of Science (Mechanical and Energy Engineering), December 2016, 98 pp., references, 31 titles.
| Identifer | oai:union.ndltd.org:unt.edu/info:ark/67531/metadc955069 |
| Date | 12 1900 |
| Creators | Dorreyatim, Mohammad |
| Contributors | Nasrazadani, Seifollah, Shi, Sheldon, Zhao, Weihuan |
| Publisher | University of North Texas |
| Source Sets | University of North Texas |
| Language | English |
| Detected Language | English |
| Type | Thesis or Dissertation |
| Format | Text |
| Rights | Public, Dorreyatim, Mohammad, Copyright, Copyright is held by the author, unless otherwise noted. All rights Reserved. |
Page generated in 0.0016 seconds