Orientador: Marco-Aurelio De Paoli / Tese (doutorado) - Universidade Estadual de Campinas, Instituto de Quimica / Made available in DSpace on 2018-08-06T15:37:34Z (GMT). No. of bitstreams: 1
Morita_AugustoTeruo_D.pdf: 5448584 bytes, checksum: b45ea2a6a097d79180fbd6e43996e982 (MD5)
Previous issue date: 2006 / Resumo: O objetivo deste trabalho foi preparar placas e parafusos auto-reforçados a partir do copolímero poli(L/DL ácido láctico), para serem utilizados na fixação interna rígida de fraturas. Este copolímero pode ser hidrolisado quando inserido no corpo humano e seus produtos de degradação são expelidos através do ciclo metabólico. Foi construído um aparelho de autoreforçamento que deve ser acoplado a uma Máquina Universal de Ensaios, capaz de orientar uniaxialmente amostras poliméricas através da passagem por uma matriz aquecida de dimensões menores que a amostra. Foram realizados ensaios prévios de auto-reforçamento com amostras de poliestireno. Ensaios de auto-reforçamento com o copolímero poli(L/DL ácido láctico) mostraram que o auto-reforçamento induziu um aumento nas propriedades mecânicas, medidas sob flexão, de ~60% no módulo de elasticidade e de ~90% na tensão máxima. A amostra moldada apresentou linhas brancas quando dobrada a temperatura ambiente, indicando a fragilização. Por outro lado, as amostras auto-reforçadas podem ser dobradas a temperatura ambiente sem que ocorresse ruptura frágil ou fragilização. Através de ensaios de difração de raios-X determinou-se que a amostra é semi-cristalina após o auto-reforçamento, apesar dos ensaios de calorimetria diferencial de varredura não identificarem positivamente a formação desta estrutura semi-cristalina. A esterilização por raios-g causa uma grande queda na massa molar, porém não altera as propriedades mecânicas. Ensaios de degradação in-vitro, com solução tampão de fosfato numa temperatura de 37 °C, das amostras esterilizadas mostraram que a massa molar sofre uma queda durante todo o ensaio de degradação e as propriedades mecânicas sofrem uma pequena queda após 15 semanas. As amostras auto-reforçadas podem ser usinadas na forma de placas e parafusos. As placas usinadas do copolímero de poli(ácido láctico) ainda podem ser dobradas a temperatura ambiente sem que ocorra quebra ou formação de linhas brancas / Abstract: In this work self-reinforced plates and screws to be used for rigid internal fixation of fractures were produced using the poly(L/DL-lactic acid) copolymer. This copolymer can be hydrolyzed when implanted in the human body and its degradation products are expelled by the metabolic cycle. A self-reinforcement module was built. It can be attached to a Universal Mechanical Testing Machine, which is capable to uni-axially orient the polymeric sample though a heated die. Initial tests of processing and self-reinforcement were conducted with polystyrene. Self-reinforcement tests were conducted with the poly(L/DL-lactic acid) copolymer. The results show that the die-drawing process induced an increase in the flexural mechanical properties of ~60% in the elastic modulus and of ~90% in the maximum tension, both measured under flexion conditions. White lines (crazing) appears when the molded sample was bent at ambient temperature, whereas the self-reinforced sample could be bent in the same conditions without fracture or sample fragilization. X-ray diffraction results indicated that the self-reinforced sample exhibits a semi-crystalline structure; notwithstanding the differential scanning calorimetry results do not conclusively identify the sample morphology. g-rays sterilization caused a decrease in the molar mass, but the mechanical properties were not affected. In-vitro degradation test were conducted at 37 °C in a buffered aqueous solution. Sterilized samples show a larger decrease in the molar mass since the beginning of the test, but the mechanical properties exhibits a smaller decrease during the test. The self-reinforced samples can be molded to the form of plates and screws. The final sample could be bent at ambient temperature without fragilization / Doutorado / Quimica Inorganica / Doutor em Ciências
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/248658 |
| Date | 15 March 2006 |
| Creators | Morita, Augusto Teruo |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, De Paoli, Marco-Aurelio, 1949-, Paoli, Marco-Aurelio De, Carbonari, Marcelo Jose, Beppu, Marisa Masumi, Longo, Cláudia, Joekes, Ines |
| Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Química, Programa de Pós-Graduação em Química |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 156p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0027 seconds