Orientador: Marco-Aurelio De Paoli / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Quimica / Made available in DSpace on 2018-08-14T18:03:39Z (GMT). No. of bitstreams: 1
Araujo_JoyceRodriguesde_M.pdf: 2541901 bytes, checksum: 06e3281cd9bd6a393831b0010bf106ed (MD5)
Previous issue date: 2009 / Resumo: As fibras naturais curtas usadas como reforço em matrizes poliméricas melhoram as propriedades mecânicas dos polímeros e podem substituir reforços inorgânicos obtidos de fontes não-renováveis como a fibra de vidro, com as vantagens adicionais de serem mais leves, menos abrasivas aos equipamentos de processamento e biodegradáveis. Na primeira etapa deste trabalho foram feitos testes para encontrar a melhor formulação e as condições ideais para se produzir compósitos de polietileno de alta densidade, PEAD, reforçados com fibras de Curauá. Para se determinar a melhor formulação foram variados: o teor de fibras no compósito, o teor e o tipo de agente de acoplamento e as condições de processamento (velocidade de rotação de rosca e perfis de temperatura durante a extrusão). A razão de aspecto e os parâmetros geométricos das fibras antes e após o processamento foram medidos através de microscopia óptica e tratados estatisticamente. A adesão entre as fases, na presença ou ausência de agente de acoplamento, foi avaliada por microscopia eletrônica de varredura. Os compósitos e os materiais puros foram caracterizados por espectroscopia de infravermelho, por métodos térmicos (termogravimetria e calorimetria exploratória diferencial) e pela medidas das propriedades mecânicas de tração, flexão e impacto. A degradação e estabilização dos compósitos foram monitoradas através do envelhecimento ambiental e acelerado das amostras com e sem aditivos estabilizantes a fim de avaliar a durabilidade dos compósitos e o efeito dos aditivos em retardar a degradação dos compósitos e homopolímeros. Conclui-se que os compósitos de PEAD reforçados com fibra de curauá tem propriedades comparáveis aos compósitos de PEAD reforçados com fibra de vidro disponíveis no mercado. / Abstract: Natural short fibers used as reinforcing agent in polymers improve their mechanical properties and may substitute inorganic reinforcing agents, produced from non renewable resources, like fiberglass, with the additional advantages of being lighter, less abrasive to the processing equipment and biodegradable. In the first part of this work the formulation and the processing conditions were studied in order to optimize the mechanical properties of the composite of high density polyethylene, HDPE, and curauá fibers. To determine the best formulation we tested: fiber content, type and content of coupling agent and processing conditions (screw rotation speed and temperature profile during extrusion). The aspect ratio and geometric parameters of the fibers before and after processing of the composites were determined by statistic treatment of the micrographies obtained by optical microscopy. The fiber/matrix phase adhesion, with and without coupling agent, was evaluated by scanning electron microscopy. The composites and the pure materials used for their preparation were characterized by fourier transform infrared spectroscopy, thermal methods (thermogravimetry and differential scanning calorimetry) and by measurement of the tensile, flexural and impact mechanical properties. The degradation and stabilization of the composites was monitored by environmental and accelerated aging tests of composite samples with and without stabilizing additives, to evaluate the durability of the composites and the effect of the additives. We conclude that HDPE composites reinforced with curauá fibers have properties comparable to commercially produced composites of HDPE reinforced with fiberglass. / Mestrado / Quimica Inorganica / Mestre em Química
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/248624 |
| Date | 08 April 2009 |
| Creators | Araujo, Joyce Rodrigues de, 1984- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, De Paoli, Marco-Aurelio, 1949-, Paoli, Marco-Aurelio De, Waldman, Walter Ruggeri, Joekes, Ines |
| Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Química, Programa de Pós-Graduação em Química |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 141 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0025 seconds