Orientadores: Luís Roberto Marcondes Martins, Regina Maria Puppin Rontani / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-18T02:16:19Z (GMT). No. of bitstreams: 1
OliveiraJunior_CarlosdaCunha_M.pdf: 1147567 bytes, checksum: ddfbf68f2d9875bfd54560350ef18e6e (MD5)
Previous issue date: 2011 / Resumo: O objetivo deste trabalho foi avaliar o efeito do acúmulo de placa na rugosidade e o da liberação de flúor de materiais restauradores na desmineralização do esmalte ao redor das restaurações. As hipóteses testadas foram que materiais liberadores de flúor promovem menor extensão da desmineralização da estrutura dental adjacente e os materiais com monômeros resinosos possuem menor rugosidade de superfície. Para este estudo in vitro, 40 blocos de esmalte dentais bovinos foram divididos aleatoriamente em 4 grupos, cada qual com 10 fragmentos dentais restaurados com diferentes materiais: cimento de ionômero de vidro modificado por resina (Vitremer), nanoparticulado (Ketac N100), cimento ionomérico convencional (Ketac Molar), compósito resinoso (Filtek Z250). Os blocos dentais foram submetidos a um modelo de desmineralização bacteriano. Em seguida, os blocos restaurados foram levados ao rugosímetro para avaliação da rugosidade a qual foi comparada com discos dos materiais testados, confeccionados como padrões de rugosidade, então, o teste de microdureza foi realizado para se obter a dureza Knoop da estrutura dentaria adjacente ao material restaurador com indentações nos pontos 50, 100 e 150 ?m de distância, nas profundidades de 10 a 120 ?m, considerando as medidas a partir de 100 ?m com valores similares ao do esmalte hígido e os valores foram convertidos em volume mineral pela fórmula de Featherstone (1983). Em seguida, foi feita a análise do conteúdo mineral da interface esmalte/restauração, após a ação dos ácidos bacterianos pela microanálise de raio-x. Os resultados mostraram que todos os grupos submetidos ao desafio cariogênico tiveram aumento significativo de rugosidade superficial. O grupo dos compósitos resinosos sofreu menor aumento significativo de rugosidade, seguida dos cimentos resinosos modificados por resina, o nanoparticulado e o convencional. Os valores de volume mineral no grupo da Z250 foi significativamente menor que os grupos com cimentos ionoméricos. A microanálise revelou conteúdo de cálcio significativamente maior nos grupos restaurados com cimentos ionoméricos. Isto permitiu concluir que os materiais com conteúdo resinoso possuem melhor polimento superficial e que o esmalte adjacente aos restauradores que liberam flúor sofreu menor desmineralização, além de apresentar maior conteúdo de cálcio / Abstract: The aim of this study was to evaluate the effect of plaque accumulation on roughness and fluoride release from dental materials on enamel demineralization around restorations. The hypothesis was that fluoride-releasing materials have lower extent of demineralization of adjacent tooth structure. For this in vitro study, 40 bovine dental enamel blocks were randomly divided into four groups, each with 10 dental fragments restored with different materials: resin-modified glass ionomer cement (Vitremer), nanoionomer (Ketac N100), conventional glass ionomer cement (Ketac Molar), resin composite (Filtek Z250). The dental blocks were subjected to a bacterial demineralization model. Then the restored blocks were taken to rugosimeter for evaluation of the roughness which was compared with discs of the tested materials, prepared as roughness patterns, then the microhardness test was performed to obtain the hardness of tooth structure adjacent to the restorative material with indentations at points 50, 100 and 150 ?m apart, at depths from 10 to 120 ?m, considering the measures from 100 ?m with values similar to sound enamel and the values were converted to mineral volume by the formula Featherstone (1983). Next step was to analyze the mineral content of enamel interface / restore, after the action of bacterial acid by x-ray microanalysis. The results showed that all groups submitted to cariogenic challenge significantly increased surface roughness. The group of composite resins has increased significantly lower roughness, followed by resin-modified resin cements, the nanoionomer and conventional. The values of mineral volume in the group of Z250 was significantly lower than groups with ionomer cements. The microanalysis showed calcium content significantly higher in groups restored with glass ionomer cements. It was concluded that materials with resin content have better polishing surface and the enamel adjacent to fluoride releasing restorative suffered less demineralization, as well as the higher calcium content / Mestrado / Materiais Dentarios / Mestre em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289736 |
| Date | 03 March 2011 |
| Creators | Oliveira Júnior, Carlos da Cunha, 1979- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Puppin-Rontani, Regina Maria, 1959-, Martins, Luís Roberto Marcondes, 1960-, Vale, Glauber Campos, Sinhoreti, Mário Alexandre Coelho |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 72 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0056 seconds