Orientadores: Júlio Roberto Bartoli, Elizabeth Grillo Fernandes / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Química / Made available in DSpace on 2018-08-22T08:51:19Z (GMT). No. of bitstreams: 1
Cecci_RicardoRodrigoRamos_M.pdf: 4182332 bytes, checksum: 4424cc557c439a1602d15a95921a2b25 (MD5)
Previous issue date: 2013 / Resumo: Nanotubos de carbono (NTCs) apresentam características interessantes para aplicações em eletrodos transparentes. Quando dispersos em escala nanométrica são transparentes ao espectro da luz visível e são capazes de conduzir eletricidade após atingirem percolação em matrizes poliméricas isolantes. Neste trabalho, é descrito o uso de nanotubos de carbono de camadas múltiplas (NTCMs) na produção de filmes poliméricos flexíveis transparentes e condutores como alternativa ao uso do óxido de índio dopado com estanho (ITO) em células solares orgânicas. Os nanotubos foram dispersos e purificados em solução aquosa de dodecil sulfato de sódio (SDS) pelos processos de sonicação e centrifugação, e a dispersão monitorada por espectroscopia UV-Vis e potencial ?. Os nanocompósitos foram produzidos via polimerização in situ do monômero metacrilato de metila (MMA) na presença de 0 a 1% p/p NTCs e os filmes depositados através da técnica de revestimento por rotação a alta velocidade (spin coating). A reação de polimerização foi acompanhada pela calorimetria exploratória diferencial (DSC). Verificou-se que na presença de NTCs, a taxa de conversão do monômero é acelerada. A cinética de degradação térmica foi avaliada pelo método de Broido utilizando a análise termogravimétrica (TGA). Foi observado que os NTCs aumentam a estabilidade térmica do PMMA, retardando a degradação por despolimerização. Estudos por espectroscopia FT-IR mostraram uma banda de absorção em 1601 cm-1, (C=C), a qual não é característica do PMMA, indicando que os NTCs participam da polimerização do PMMA. Para concentrações de até 1% p/p de NTCs, os filmes PMMA/NTC apresentaram excelentes propriedades ópticas. Ou seja, baixo coeficiente de absorção, na ordem de 103 cm-1, altos valores de gap óptico (Eopt), entre 3,2 e 4,14 eV, e alta transparência por todo espectro visível, entre 88 e 93%. Nas mesmas concentrações, foi observada uma diminuição substancial na resistividade elétrica dos filmes em 8 ordens de grandeza (de 1016 para 108 ?/quadrado), comparados ao filme de PMMA puro. Entretanto, a faixa de resistividade alcançada ainda é típica de materiais isolantes. Estudos de otimização poderiam originar filmes PMMA/NTC como uma alternativa promissora para ITO em OPVs / Abstract: Carbon nanotubes (CNTs) have interesting features for applications in transparent electrodes. When dispersed at the nanoscale, they become transparent within the visible range and are able to conduct electricity after reaching the percolation threshold in an insulating polymer matrix. In this work, the use of multi-walled carbon nanotubes (MWCNTs) is described for the production of flexible transparent conducting polymer films as an alternative to the use of indium-tin oxide (ITO) in organic solar cells. The nanotubes were dispersed and purified in an aqueous solution of sodium dodecyl sulfate (SDS) by the process of sonication and centrifugation, and the dispersion monitored by UV-Vis spectroscopy and ? potential. The nanocomposites were produced via in situ polymerization of the monomer methyl methacrylate (MMA) in the presence of 0 to 1 %wt. of CNTs. The films were deposited by the spin-coating technique. The polymerization reaction was monitored by differential scanning calorimetry (DSC). It was found that in the presence of CNTs, the conversion rate of the monomer is accelerated. The kinetics of thermal degradation was measured according to the Broido's method by using thermogravimetric analysis (TGA). It was observed that CNTs increase the thermal stability of PMMA, slowing degradation by depolymerization. FT-IR data showed an absorption band at 1601 cm-1 (C = C), which is not characteristic of PMMA, indicating that the CNTs takes place in the polymerization of PMMA. For concentrations up to 1wt% of CNTs, the PMMA/CNT films had excellent optical properties, i.e., a low absorption coefficient in the order of 103 cm-1, wide optical gap (Eopt) between 3.2 and 4.14 eV, and high transparency within the whole visible range, between 88 and 93%. In the same concentrations, the electrical resistivity of the films dropped by 8 orders of magnitude (from 1016 to 108 ?/sqr), compared to the pure PMMA film. Even though this electrical resistivity value is typical of insulating materials, further optimization studies could provide PMMA/CNT films as a promising alternative to ITO in OPV / Mestrado / Ciencia e Tecnologia de Materiais / Mestre em Engenharia Química
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/266636 |
| Date | 22 August 2018 |
| Creators | Cecci, Ricardo Rodrigo Ramos |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Fernandes, Elizabeth Grillo, Bartoli, Julio Roberto, 1954-, Campos, João Sinézio de Carvalho, Gonçalves, Agnaldo de Souza |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Química, Programa de Pós-Graduação em Engenharia Química |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 109 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0524 seconds