Previous issue date: 2016-07-04 / Conselho Nacional de Desenvolvimento Científico e Tecnológico / A proposta desse trabalho foi avaliar a aplicação de polissulfetos na polpação kraft em diferentes proporções de cavacos de Eucalyptus spp. (E) e Pinus spp. (P). Amostras de cavacos dessas espécies foram caracterizadas quanto à composição química, densidade básica e aparente. Utilizou-se misturas de cavacos em três diferentes percentuais em peso, 50E/50P, 70E/30P e 90E/10P, as quais foram processadas tendo como objetivo o número kappa 19±0,5, pelos processos kraft convencional, sem o uso do aditivo, que foram usadas como referência, e kraft-polissulfetos (kraft-Sn), com adição de 1,5 e 3,0% de Sn, base madeira; totalizando nove tratamentos. As polpas marrons foram branqueadas pela sequência OD(EP)D, até alvura de 85% ISO, refinadas em moinho PFI (1.000, 2.000 e 3.000 revoluções) e avaliadas quanto às suas propriedades físico-mecânicas. Os resultados mostram que o uso do aditivo Sn (1,5 ou 3%), preservou hemiceluloses, aumentou o rendimento e a viscosidade das polpas e reduziu o fator H, em todas as proporções de madeiras utilizadas. A eficiência da deslignificação com oxigênio foi mais alta para misturas de madeira contendo maior proporção de Pinus spp e não foi influenciada de maneira clara pelo uso do aditivo Sn. As diferentes misturas de madeira bem como o uso do Sn no cozimento não influenciaram de maneira clara e significativa o consumo de reagentes de branqueamento. A refinabilidade das polpas oriundas de cozimentos com Sn foram superiores às das polpas referências, sendo as misturas de madeiras, contendo maior proporção de eucalipto, mais fáceis de refinar. O índice de arrebentamento e rasgo têm suas propriedades melhoradas à medida que é adicionado Pinus às misturas, e o índice de tração e opacidade são prejudicados com esse aumento. Não houve efeito significativo das misturas na resistência à passagem de ar. O uso do aditivo Sn no cozimento melhorou as resistências à tração e ao rasgo das polpas, mas afetou negativamente as suas opacidades. Não houve efeito significativo do Sn no índice de rasgo e na resistência à passagem de ar. / The purpose of this study was evaluate polysulfides application in the kraft pulping at different proportions of Eucalyptus spp. (E) and Pinus spp. (P) chips. These species were characterized for chemical composition, basic and bulk density. Was used three different mixtures done by weight percentages, 50E/50P, 70E/30P and 90E/10P, which were pulped to kappa number 19 ± 0.5, by conventional kraft processes with no additives , which were used as a standard, and kraft-polysulfides (kraft-Sn), with addition of 1.5 to 3.0% Sn, based on dry wood; totaling nine treatments. Brown pulps were bleached by the sequence OD(EP)D until whiteness of 85% ISO, refined in PFI mill (1,000, 2,000 and 3,000 revolutions) and evaluated for their physical and mechanical properties. The results shown that the Sn addition (1,5 or 3%), preserves hemicelluloses, increasing yields, reducing pulp viscosity and the H Factor, in all chips proportions used. The oxygen delignification efficiency was higher for mixtures with higher pine proportion and the Sn effect of was not clearly established. Bleaching chemicals consumption was not influenced by different chip proportion neither by Sn addition. The polysulfide pulp refining was easier than standard pulp refining, as the higher was the Eucalyptus proportion easier was the pulp refining. . The burst and tear index have their properties improved with pine addition to the mixture, however for tensile index and opacity the effect was the opposite . There was no significant effect of mixtures in the air passage resistance. The Sn additive use in cooking has improved tensile and tear of the pulps, but negatively affected their opacities. There was no significant effect of Sn in tear index and the air passage resistance.
Identifer | oai:union.ndltd.org:IBICT/oai:localhost:123456789/8360 |
Date | 04 July 2016 |
Creators | Zanão, Marina |
Contributors | Oliveira, Rubens Chaves de, Colodette, Jorge Luiz |
Publisher | Universidade Federal de Viçosa |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Source | reponame:Repositório Institucional da UFV, instname:Universidade Federal de Viçosa, instacron:UFV |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0147 seconds