Understanding the role of kinetic parameters on the crystallization of miscible semicrystalline polymer blends

This dissertation discusses results of crystallization kinetic, morphology and scattering studies on miscible semi crystalline blends of poly(pivalolactone)/ poly(vinylidene fluoride)(pPVLIPVF₂) and poly(pivalolactone)/poly(vinylidene fluoride <i>co</i>- tetrafluoroethylene)(95-5) (PPVL/P(VF2-TFE)(95-5)) prepared by solution blending. The spherulitic growth rates of the α-phase PPVL from miscible blends with PVF₂ or P(VF₂- TFE)(95-5) were measured by polarized optical microscopy as a function of blend composition and isothermal crystallization temperature, Tx, between 160°C and 215.5°C. The PPVL weight fraction in the blends ranged from 100 to 10 wt%. Using the Lauritzen-Hoffman kinetic theory of polymer crystal growth, the equilibrium melting temperatures of the α-phase PPVL in both the PPVL/PVF₂ and the PPVL/P(VF₂-TFE)(95-5) blends have been determined, for the first time, directly from the spherulitic growth rate data. Analysis of the composition dependence of the nucleation constant, Kg suggests that the α-phase PPVL crystal/melt lateral interface free energy, Ï , in the blends decreases markedly with increasing PVF₂ or P(VF₂-TFE)(95-5) concentration. / Ph. D.

Identiferoai:union.ndltd.org:VTETD/oai:vtechworks.lib.vt.edu:10919/40312
Date10 November 2005
CreatorsHuang, Jiang
ContributorsChemistry, Marand, Hervé L., Gibson, Harry W., Riffle, Judy S., Wightman, James P., Wilkes, Garth L.
PublisherVirginia Tech
Source SetsVirginia Tech Theses and Dissertation
LanguageEnglish
Detected LanguageEnglish
TypeDissertation, Text
Formatxiii, 167 leaves, BTD, application/pdf, application/pdf
RightsIn Copyright, http://rightsstatements.org/vocab/InC/1.0/
RelationOCLC# 34348067, LD5655.V856_1995.H835.pdf

Page generated in 0.0018 seconds