Nano-cellulose fibers/suspension has very high viscosity, its viscosity has to be lower before it can be applied in the paper coating recipe. For this purpose the adsorption behaviour of polyvinyl alcohol on nano-cellulose fibers were investigated using method developed by Zwick in 1960, based on the formation of PVA-iodide blue complex in the presence of boric acid. The experiments showed that the maximum adsorbed amount i.e. 0.13 g PVA/g NFC was obtained in a dispersion with 0.2 % PVA concentration. It should be possible to further increase the PVA adsorption as the adsorbed amount didn’t reach a saturation point where the PVA adsorption attained a constant value. It was also found that adsorption of PVA on NFC is time dependent. The absorbance measurement after four days of mixing PVA/NFC suspension showed only partially adsorption of PVA on nano-cellulose surface. An equilibrium time of 10-13 days was needed for PVA to fully adsorb on nano-cellulose fibers surface. Another important observation was that PVA adsorption also depends on the concentration of nano-cellulose fibers. A lower concentration of NFC easily allows PVA to adsorb on its surface, as compared to higher NFC concentration. An important finding during the methodology development was the method to get rid of formation of flocs in the blue iodide complex solution; by slowly addition of reactants, especially the KI/I2 solution under continuous stirring around 60oC the tendency to flocs formation was suppressed.
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kau-6720 |
| Date | January 2010 |
| Creators | Hussain, Arif |
| Publisher | Karlstads universitet, Fakulteten för teknik- och naturvetenskap |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0023 seconds